Tuning the Pore Environment of MOFs toward Efficient CH 4 /N 2 Separation under Humid Conditions
Tong Li,Xiaoxia Jia,Hui Chen,Zeyu Chang,Libo Li,Yong Wang,Jinping Li
DOI: https://doi.org/10.1021/acsami.2c01156
2022-03-23
Abstract:Adsorption separation technology using adsorbents is promising as an alternative to the energy-demanding cryogenic distillation of natural gas (CH4/N2) separation. Although a few adsorbents, such as metal–organic frameworks (MOFs), with high performance for CH4/N2 separation, have been reported, it is still challenging to target the desired adsorbents for the actual CH4/N2 separation under humid conditions because the adsorption capacity and selectivity of the adsorbents might be mainly dampened by water vapor. Except for the high CH4 uptake and CH4/N2 selectivity, the adsorption material should simultaneously have excellent stability against moisture and relatively low-water absorption affinity. Here, we tuned the ligands and metal sites of reticular MOFs, Zn-benzene-1,4-dicarboxylic acid–1,4-diazabicyclo[2.2.2]octane (Zn-BDC–DABCO) (DMOF), affording a series of isostructural MOFs (DMOF-N, DMOF-A1, DMOF-A2, and DMOF-A3). Because of the finely engineered pore size and introduced aromatic rings in the functional DMOF, gas sorption results reveal that the materials show improved performance with a benchmark CH4 uptake of 37 cm3/g and a high CH4/N2 adsorption selectivity of 7.2 for DMOF-A2 at 298 K and 1.0 bar. Moisture stability experiments show that DMOF-A2 is a robust MOF with low water vapor capacity even at ∼40% relative humidity (RH) because of the presence of more hydrophobic aromatic rings. Breakthrough experiments verify the excellent CH4/N2 separation performances of DMOF-A2 under high humidity.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c01156.Lowest-energy frames for the CH4 molecular adsorption in DMOF at 298 K and infinite dilution (AVI)Lowest-energy frames for the CH4 molecular adsorption in DMOF-A2 at 298 K and infinite dilution (AVI)SEM images; XPS spectra; TGA curves; gas adsorption isotherms at 313 K; gas selectivity coefficient at 313 and 273 K; fitting adsorption isotherms and parameters of the dual-Langmuir–Freundlich for gas adsorption; comparison of gas separation performance of some typical adsorbents; illustration of the most favored gas adsorption site in DMOF and DMOF-A2; PXRD patterns for DMOF-A1, DMOF-A2, and DMOF-A3 treated under different conditions; breakthrough experimental setup schematic; and breakthrough curves of DMOF and DMOF-A2 for the CH4/N2 mixture (80/20, v/v) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology