Irreversible microstructural changes of calcium silicate hydrate during the first drying-resaturation cycle

Jianhao Yin,Wenyu Li,Jian Wang,Xiangming Kong

DOI: https://doi.org/10.1016/j.cemconres.2022.107032

IF: 11.958

2023-01-01

Cement and Concrete Research

Abstract:Calcium silicate hydrate (C-S-H) is the most important hydration product of Portland cement. In this study, a brand-new compacting method based on pozzolanic reaction was used to prepare pure C-S-H block samples. Compressive strength and flexural strength of the C-S-H samples were tested. Water desorption-absorption be-haviors of the C-S-H during the first drying-resaturation (D-R) cycle were measured by means of thermogravi-metric analysis and low field 1H NMR relaxometry (LF-NMR). A significant irreversible reduction of gel pore volume was detected after D-R cycle, while volume of interlayer pores remained unchanged. Based on results, gel pores were classified into collapsible gel pore (CGP, >2.6 nm), deformable gel pore (DGP, 1.4-2.6 nm) and rigid gel pore (RGP, <1.4 nm). RGPs are stable both in size and volume. DGPs are stable in pore volume but irre-versibly changeable in pore size and CGPs are vulnerable and largely collapse causing reduction of pore size and volume after the first drying.