From Symmetry Breaking to Unraveling Chirality of Metal Nanoclusters
Guocheng Deng,Sami Malola,Juanzhu Yan,Ying-Zi Han,Peng Yuan,Chaowei Zhao,Xiting Yuan,Shuichao Lin,Zichao Tang,Boon K. Teo,Hannu Häkkinen,Yingzi Han,Nanfeng Zheng
DOI: https://doi.org/10.1002/ange.201800327
2018-01-01
Abstract:A general method, using mixed ligands (here diphosphines and thiolates) is devised to turn an achiral metal cluster, Au13Cu2, into an enantiomeric pair by breaking (lowering) the overall molecular symmetry with the ligands. Using an achiral diphosphine, a racemic [Au13Cu2(DPPP)3(SPy)6] + was prepared which crystallizes in centrosymmetric space groups. Using chiral diphosphines, enantioselective synthesis of an optically pure, enantiomeric pair of [Au13Cu2((2r,4r)/(2s,4s)-BDPP)3(SPy)6] + was achieved in one pot. Their circular dichroism (CD) spectra give perfect mirror images from 250-500nm with maximum anisotropy factors of 1.2 × 10. Density Functional Theory (DFT) calculations provided good correlations with the observed CD spectra of the enantiomers and, more importantly, revealed the origin of the chirality. Racemization studies show high stability (no racemization at 70°C) of these chiral nanoclusters, which hold great promise in applications such as asymmetry catalysis. Chirality is ubiquitous in nature 2] and plays a key role in enantioselective catalysis, pharmaceutical sciences, optical devices, etc. In the past few decades, people have established lots of chemical means for enantioselective synthesis of chiral molecules for specific applications. To date, many chiral nanoclusters have been discovered or synthesized. Atomically precise nanoclusters are particularly good models to probe the origin of chirality. Many efforts have been dedicated to unraveling the chirality in cluster science and several plausible mechanisms have been proposed such as the dissymmetric field effect and chiral footprint model. However, unlike chiral organic compounds or other small molecules, asymmetric synthesis of large chiral structures such as nanoparticles or nanoclusters remains a real challenge, which hampers the progress of unraveling chirality of metal nanoclusters. Generally speaking, chiral nanoclusters can be classified into three broad categories by different origins of the chirality: (1) chiral metal core; (2) asymmetry arrangement of achiral surface structure (such as RS-Au-SR unit); (3) homochiral ligands induced extrinsic chirality. Some chiral clusters may belong to two of the three categories, e.g., with chirality originating from both staple and kernel. 23] Symmetry breaking is a universal phenomenon in nature and the concept of symmetry breaking in the present context includes spontaneous resolution, chirality amplification, chiral induction, asymmetric catalysis, crystal growth, or combinations thereof. 25] Since most metal clusters have an achiral, highly symmetrical metal core (often possessing mirror or inversion symmetries), the simplest method to synthesize a chiral metal cluster is to lower the overall symmetry with the ligands. However, symmetry breaking by asymmetry arrangement of achiral ligands is often difficult to control. Furthermore, it inevitably leads to racemic mixtures. Many efforts have been made to enantioseparate those racemic mixtures by using chiral HPLC columns and phase transfer method using a chiral ammonium salt. The problem here is that it is often challenging to carry out such separations to produce optically pure nanoparticles. Moreover, racemization can exist in chiral metal cluster systems. For example, racemization studies on thiolate-protected gold cluster have been done by Bu ̈rgi’s group. They found the gold−thiolate interface is flexible and racemization phenomenon have been observed at 30°C. 31] Herein we report the syntheses of three closely related, extrinsically chiral metal nanoclusters via these two strategies. The first is a racemate, characterized as [Au13Cu2(DPPP)3(SPy)6] (2), which has an achiral metal core, six Spy, and three achiral diphosphine ligands DPPP in asymmetric arrangements (where Spy= pyridine-2-thiol and DPPP=1,3bis(diphenyphosphino)propane). Using chiral (2r,4r)/(2s,4s)-2,4bis(diphenylphosphino)pentane (BDPP) (Figure S1) in place of achiral diphosphine, two optically pure enantiomers [Au13Cu2(2r,4r-BDPP)3(SPy)6] (3-R) and [Au13Cu2(2s,4sBDPP)3(SPy)6] (3-S), were obtained in one pot. All the three clusters were synthesized by reducing a mixture of Au, Cu, pyridinethiol and diphosphine with NaBH4 in an ice bath (see Supporting Information (SI) for more details). Single crystals suitable for X-ray diffraction were grown by slow solvent evaporation after ten days. Single-crystal structure determination revealed that 2 is a racemate crystallized in the centrosymmetric space group P21/c. The unit cell comprises two pairs (Z = 4) of enantiomers (Table S1 and Figure S2). As shown in Figure 1a, the molecular architecture of 2 is similar to the previously reported [Au13Cu2(PPh3)6(SPy)6] (1, depicted in Figure S3). As shown in Figure 1b and c, 2 has an icosahedral Au13 core and two Cu atoms capping two Au3 triangles of the icosahedral Au13 core oriented along one of the 3-fold axes of the icosahedral Au13. The core of 2 is achiral and displays D3d symmetry. The six pyridine2-thiol ligands bind to the two Cu atoms and six gold (one each) atoms from the two Au3 triangles capped by Cu as bidentate ligands (Figure 1a). The pyridine-2-thiol ligands in two sides of the metal core rotate some degree (Figure 1d and Table 4). The pyridine-2-thiol ligands are in asymmetry arrangement and displays C3 symmetry. So the symmetry of this cluster is effectively lowered here. Three DPPP ligands bind to six Au atoms at the ‘equatorial’ positions of the icosahedral core. As shown in Figures 1e, the three DPPP ligands cap on the cluster [a] G. C. Deng, J. Z. Yan, Y. Z. Han, P. Yuan, Dr. C. W. Zhao, X. T. Yuan, Dr. S.C. Lin, Prof. Z. C. Tang, Prof. B. K. Teo, Prof. N. F. Zheng State Key Laboratory for Physical Chemistry of Solid Surfaces, Collaborative Innovation Center of Chemistry for Energy Materials, and Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University Xiamen 361005, China E-mail: nfzheng@xmu.edu.cn boonkteo@xmu.edu.cn [b] Dr. S. Malola, Prof. H. Häkkinen Departments of Physics and Chemistry Nanoscience Center, University of Jyväskylä Jyväskylä 40014, Finland Supporting information for this article is available on the WWW under http:// 10.1002/anie.201800327 A cc ep te d M an us cr ip t Angewandte Chemie International Edition This article is protected by copyright. All rights reserved.