Investigation on Surface Metallic Active Structure of Supported Ruthenium Catalyst
Ding Yunjie,Liang Dongbai,Lin Liwu,Li Can,Xin Qin
DOI: https://doi.org/10.3866/PKU.WHXB19930608
1993-01-01
Acta Physico-Chimica Sinica
Abstract:The metallic surface structure of supported Ru catalysts, activated at different pretreatment conditions, was investigated by following the development of IR bands due to adsorbed CO, as well as by following the methane formation in temperature-programmed surface reaction (TPSR-MS) of adsorbed CO in a H-2 flow. It revealed that there existed three kinds of active sites, designated as S-1, S-2 and S-3 sites,respectively. The S-1 sites, characterized by low frequency (LF) bands of 1980 similar to 2060cm(-1) for linearly adsorbed CO, were attributed to metallic Ru particles with almost no interaction with the support. The TPSR-MS results showed that, when reaction with H-2, the adsorbed CO on these sites changed into CH4 at a lower temperature of ca. 450K, varying with activated conditions. On the other hand, the S-2 sites were visualized to be interfacial Ru particles in direct contact with supporting materials, and exhibited stronger interaction with support. As a result of this MSI effect, the S-2 sites would result in the formation of electron-deficient Ru delta+ sites, and maintain high dispersive states of metal catalysts, and also adsorb CO with configuation of Ru delta+-CO at 2075 +/- 5cm(-1) medium frequency (MF2). Upon hydrogenation, the adsorbed CO formed methane at a much higher temperature of ca. 650K. Obviously, the S-1 and S-2 sites are static sites of the conventional nature. The interaction of CO with supported Ru catalyst led to the oxidative disruption of soluble surface Ru atoms or clusters with coordinatively unsaturation on the S-1 sites, as indicated by the slow transformation of the bands at 1980 similar to 2060cm(-1) due to Ru-x(o)-CO to bands at 2153 +/- 5cm(HF) and 2075 +/-(MF1)cm(-1) attributed to surface-anchored carbonyl [(support-O)(2)Ru(CO)(3)](n) (n=1,2 ... ) species, referred to as S-3 sites. The oxidative corrosive carbonylation of Ru is both favored thermodynamically and feasible kinetically under our experimental conditions. It was demonstrated that at higher temperature, the presence of CO, especially with high partial pressure of hydrogen, such as in the case of TPSR-MS experiments, causes the reductive agglomeration of the S-3 sites, and the soluble Ru particles or clusters on the S-1 sites will be restored. These observation led us to postulate that the S-3 sites were active sites formed dynamically during the course of the Fischer-Tropsch reaction.