Straightforward Preparation of Ca-bentonite/polymer Nanocomposite by Confining Salt-Resistant Copolymers into Montmorillonite Interlayers

Hui Wang,Chongrui Zhang,Lusha Jiang,Shan Tong,Yu-Chao Li,Hefu Pu,Qiang Zhao
DOI: https://doi.org/10.1016/j.polymer.2022.125519
IF: 4.6
2022-01-01
Polymer
Abstract:Calcium bentonites (CaB), rich in European and Asian countries, are potential barrier materials for landfill leachate containment. However, CaB has to be converted into sodium bentonite (NaB) by Na-activation so as to facilitate intercalation modification. In this study, salt-resistant poly(acrylic acid-N, N-diethyl acrylamide) [P (AA-DEA)] was designed to intercalate and graft CaB by in situ polymerization without prior Na-activation. By this design, acrylic acid monomers were first adsorbed into interlayers of Ca-montmorillonite (Ca-MT) through the electrostatic complexation with Ca2+, dislodging Ca2+ from montmorillonite surfaces. Then, ammonium ions of N, N-diethyl acrylamide were adsorbed into Ca-MT interlayers. Swelling index of the obtained CaB/P(AA-DEA) nanocomposite in aggressive coal combustion product (CCP) leachate is 15.8 mL/2g, which is as high as 3.4 times that of CaB. CaB/P(AA-DEA)-based geosynthetic clay liners (GCLs) exhibit very low hydraulic conductivity (1.6x10-12 m/s) to CCP leachate, which is as low as 3.3% that of the U.S. standard requirement and similar to 4 orders of magnitude lower than that of CaB-based GCL. Polymer elution of CaB/P(AA-DEA)-8% in CCP leachate is as low as 1.9% that of the dry mixed samples.
What problem does this paper attempt to address?