Abstract:Polyimide (PI)-silica composite membranes and their derived carbon-silica composite membranes were prepared for gas separation. The polyimide-silica composite membranes were prepared using the sol-gel technique, in which the polyimide matrix was synthesized by the condensation of pyromellitic dianhydride (PMDA) and 4,4'-oxydianiline (ODA) while the inorganic phase was prepared by the in situ hydrolysis of tetraethyl orthosilica (TEOS) and a silane coupling agent, (3-aminopropyl)triehtoxysilane (APTES). The derived carbon-silica composite membranes were prepared by the pyrolysis of the polyimide-silica composite membranes at 900 degrees C under vacuum. The structures of the membranes were characterized by scanning electron microscopy (SEM), energy dispersive X-ray (EDX) spectroscopy, and X-ray diffraction (XRD) technique. The gas (He, CO2, N-2 and O-2) permeabilities of the polyimide-silica composite membranes and carbon-silica composite membranes were investigated. With the introduction of the silica, there was no significant enhancement of the gas separation in the resulting polyimide-silica composite membranes over the polyimide membrane, which still suffered a "trade-off" relationship between permeability and selectivity. However, the derived carbon-silica composite membranes exhibited better gas separation properties. The C-SiO2 28% composite membrane produced the highest permeances of 1042.18, 991.21, 296.03 and 155.26 GPU for He, CO2, O-2 and N-2, respectively, which were 21.61, 137.67, 103.15 and 150.74 times, respectively, of those of the pure carbon membrane. The C-SiO2 11% composite membrane produced the highest selectivities of 37.57, 36.61 and 7.09 for He/N-2, CO2/N-2 and O-2/N-2, respectively, which had surpassed the Robeson's upper bound for these gas pairs. The agreement between the pure gas selectivity and the mixed gas selectivity for O-2/N-2 gas pair was reasonable, ranging from -8.30% to +16.61% using the pure gas selectivity as the base except for C-SiO2 23% composite membrane which showed +35.81% difference. (C) 2013 Elsevier B.V. All rights reserved.

Gas Separation Performance of Polyimide Homogeneous Membranes Containing tert-Butyl Groups

Novel Semi-Alicyclic Polyimide Membranes: Synthesis, Characterization, and Gas Separation Properties

Aromatic Polyimide Membranes with tert-Butyl and Carboxylic Side Groups for Gas Separation Applications—Covalent Crosslinking Study

Intrinsically Microporous Polyimides Derived from 2,2′-Dibromo-4,4′,5,5′-bipohenyltetracarboxylic Dianhydride for Gas Separation Membranes

PERVAPORATION SEPARATION FOR TOLUENE/n-HEPTANE MIXTURE BY POLYIMIDE MEMBRANES CONTAINING FLUORINE

Surface Modification of Polyimide Membranes by Diamines for H-2 and Co2 Separation

Synthesis and gas separation properties of polyimide membranes derived from oxygencyclic pseudo-Tröger's base

Acetate-Functional Thermally Rearranged Polyimides Based on 2,2-Bis(3-amino-4-hydroxyphenyl)hexafluoropropane and Various Dianhydrides for Gas Separations

Thermally Rearranged Polymer Membranes Containing Highly Rigid Biphenyl Ortho-Hydroxyl Diamine for Hydrogen Separation

Six-membered Ring Copolyimides As Novel High Performance Membrane Materials for Gas Separations

Experimental study on physical properties and pervaporation performances of polyimide membranes

From a hyperbranched polyimide to a microporous network polyimide via reaction temperature change and its application in gas separation membranes

High-strength, Soluble Polyimide Membranes Incorporating Tröger’s Base for Gas Separation

Synthesis of Polyimides Containing Fluorine and Their Pervaporation Performances to Aromatic/Aliphatic Hydrocarbon Mixtures

Highly Selective Benzimidazole-Based Polyimide/Ionic Polyimide Membranes for Pure- and Mixed-Gas CO2/CH4 Separation

Gas permeation properties of hyperbranched polyimide membranes

Synthesis, characterization, and gas separation properties of novel fluorinated co-polyimides with bulky side groups

Hydrogen bonding-induced 6FDA-DABA/TB polymer blends for high performance gas separation membranes

Gas Sorption, Diffusion, and Permeation in Thermally Rearranged Poly(Benzoxazole-Co-Imide) Membranes

Preparation and characterization of polyimide–silica composite membranes and their derived carbon–silica composite membranes for gas separation

Synthesis of new copolyimides containing pyridine and morpholine groups for gas separation through molecular design and simulation