Abstract:A high-quality joint of pressureless sintered SiC ceramic (PS-SiC) and stainless steel brazed by AgCu/AgCuTi brazing alloy was realized. The effects of brazing temperature and holding time on the interfacial microstructure and mechanical properties of PS-SiC-stainless steel were analyzed. During brazing, Fe and Cr diffused into a brazing seam, and the typical interfacial microstructure of joints brazed at 890 degrees C for 15 min was stainless steel/Cr5Si3 + FeSi2 + Ag(s,s)/Cr5Si3 + FeSi2 + Ag(s,s) + Cu(s,s) + TiSi2 + TiC/FeSi2 + Ag(s,s) + Cu(s,s) + TiSi2/Ag(s,s) + Cu(s,s) + SiC/PS-SiC ceramic. Cu-Fe system improved the toughness of the joint, and the shear strength of the joint increased to similar to 67 MPa. With increasing brazing temperature and holding time, the element Fe continued diffusing into the brazing seam, and the uniformity of Cu-Fe system became worse. Then Cu(s,s) infiltrated into the surface layer of PS-SiC ceramic and FeSi2 brittle phase gathered in the brazing seam. Then, the brittleness of the joint increased and the shear strength of the joint decreased.

Interfacial Microstructure and Mechanical Properties of Pressureless Sintered SiC Ceramic and Stainless Steel Joints Brazed by AgCu/AgCuTi Alloy