Synthesis and Optical Properties of Mn4+ Activated Double-Perovskite Niobate Deep Red Phosphors for WLEDs and Plant Cultivation

Yanan Li,Hu Wang,Xiaoyi Liu,Guixia Liu,Jinxian Wang,Dan Li,Wensheng Yu,Xiangting Dong

DOI: https://doi.org/10.1016/j.mtcomm.2022.104817

IF: 3.8

2022-01-01

Materials Today Communications

Abstract:Mn4+ doped oxides red phosphors have great potential for white-light-emitting diodes (WLEDs) and plant growth light. Herein, deep red phosphors Ba2LuNbO6:xMn4+ with perovskite structure were synthesized by solid state method in air atmosphere. The crystal structure, morphology, composition and optical properties of Ba2LuNbO6: Mn4+ phosphors were systematically studied by X-ray diffraction, Rietveld refinement, SEM and EDS and pho-toluminescence spectra. Under excitation by 380 nm NUV light, the phosphor emitted bright red light around 670 nm and far-red light around 697 nm owing to the spin-forbidden 2Eg -> 4A2 g transition of Mn4+ ions. Temperature-dependent photoluminescence spectra confirmed the high thermal stability of Mn4+-activated Ba2LuNbO6 phosphors. The fluorescence intensity maintained about half of the initial intensity at 400 K, and the thermal quenching was due to the increase of non-radiative transitions at high temperature. Finally, LED devices were fabricated using 365 nm NUV chips with commercial blue, green phosphors and Ba2LuNbO6:Mn4+ red phosphors for the use of outdoor lighting, which had color rendering index (CRI) of 84.4 and color temperature (CCT) of 5710 K. The results indicate that Ba2LuNbO6:Mn4+ phosphors have great potential as a deep red phosphor in the field of WLEDs and plant growth light.