Fabrication of Superhydrophobic Coatings by Low-Temperature Sintering of Ag Nanoparticle Paste

Chenghao Zhang,Chun Li,Mushi Zheng,Xiaoqing Si,Dejun Gao,Junlei Qi,Jian Cao

DOI: https://doi.org/10.1016/j.mtcomm.2022.104705

IF: 3.8

2022-01-01

Materials Today Communications

Abstract:Ag nanoparticle paste was used to fabricate mechanically durable superhydrophobic surfaces via sintering. A facile method was first adopted to synthesize the Ag nanoparticle paste. To obtain multi-level hierarchical superhydrophobic surfaces, a stainless steel mesh was introduced to the sintering process of the Ag nanoparticle paste. The morphology of the steel mesh was replicated onto the Ag surface under sintering pressure, forming a first-level surface roughness. Using low-temperature sintering, a bond was created between the Ag nanoparticles, enhancing the mechanical durability of the as-prepared surfaces. The gap between the Ag nanoparticles was retained under low pressure, leading to a high surface roughness, which is beneficial for preparing super -hydrophobic surfaces. After modification with stearic acid, the as-fabricated Ag coatings exhibited good superhydrophobicity, long-term durability, and mechanical stability. The superhydrophobic Ag coatings can also be fabricated on different substrates successfully. Thus, this type of superhydrophobic coating has promising prospects in practical applications.