In Situ Exsolved Core-Shell Nanoparticles on Perovskite Parent: A Novel High-Performance Anode for Solid Oxide Fuel Cells
Nianjun Hou,Yicheng Zhao,Yongdan Li
DOI: https://doi.org/10.1149/ma2018-01/32/1966
2018-04-13
ECS Meeting Abstracts
Abstract:Solid oxide fuel cells (SOFCs) with a high energy conversion efficiency and low emissions are considered as promising substitutes for traditional thermal power devices [ 1 ,2] . However, the conventional Ni based anode suffers from agglomeration, sulfur poisoning and carbon coking with hydrocarbon fuels, which limit its application [3] . Various alternative materials have been studied as promising SOFC anodes. Meanwhile, in situ exsolution has been developed as a fabrication strategy to prepare perovskite oxides with uniformly dispersed nanometallic particles [4] . Recently, A-site ordered PrBaMn 2 O 5+d has been reported as a promising anode with high electrical conductivity and good catalytic activity for the electrochemical oxidation of both hydrogen and hydrocarbons [5] . In this work, La 0.5 Ba 0.5 Mn 1-2x Co x Fe x O 3-δ (x=0, 0.05, 0.1) has been synthesized with the Pechini method and investigated as an anode material of SOFCs with H 2 and methane as fuels. The structure of the anode converts from a mixture of cubic and hexagonal phases to a perovskite structure with core-shell nanoparticles on the surface after reduction. The in situ exsolution process of the metals on the B sites is studied with an X-ray photoelectron spectrometer, a thermogravimetric analyzer and a transmission electron microscope. The results of the electrochemical tests demonstrate that the doping of Co and Fe into B sites effectively improve the performance of the single cell with H 2 as the fuel. A single cell with a 2CF-LBM anode layer and a 300-μm La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ electrolyte layer exhibits a maximum power density ( P max ) of 98, 210, 383, 653 and 1479 mW cm -2 with wet H 2 as the fuel at 650, 700, 750, 800 and 850 o C, respectively, and achieves a peak power density of 503 mW cm -2 at 850 o C when fueled with wet CH 4 . Moreover, the 2CF-LBM anode exhibits a high coking resistance, and no remarkable degradation of the performance is observed when the cell is operated with methane as the fuel for more than 200 hours. Keywords: Solid oxide fuel cell; Perovskite; Anode; In situ exsolution Table 1. Abbreviations of various anode materials and the maximum output power densities of the cells fed with H 2 and CH 4 at 850 o C Anode composition Abbreviation P max,H2 (mW cm -2 ) P max,CH4 (mW cm -2 ) La 0.5 Ba 0.5 MnO 3-δ LBM 962 336 La 0.5 Ba 0.5 Mn 0.9 Co 0.05 Fe 0.05 O 3-δ 1CF-LBM 1241 389 La 0.5 Ba 0.5 Mn 0.8 Co 0.1 Fe 0.1 O 3-δ 2CF-LBM 1479 503 Figure 1. (a) Bright-field TEM image, (b) HAADF imagine with the EDS linear scanning and (c) EDS elemental map of the reduced 2CF-LBM; (d) I-V and I-P curves of the single cell in 650-850 o C with H 2 as fuel. References S. Tao, J.T. Irvine, Nature materials 2003, 2 , 320-323. Z. Shao, S.M. Haile, Nature 2004, 431 , 170-173. X.M. Ge, S.H. Chan, Q.L Liu, et al., Advanced energy materials 2012, 2 , 1156-1181. D. Neagu, G. Tsekouras, D. N. Miller, et al., Nature Chemistry 2013, 5 , 916-923. S. Sengodan, S. Choi, A. Jun, et al., Nature materials 2015, 14 , 205-209. Figure 1