In Situ Three-Dimensional Welded Nanofibrous Membranes for Robust Membrane Distillation of Concentrated Seawater
Lingling Zhong,Liuqian An,Yu Han,Zhigao Zhu,Dongqing Liu,Dongmei Liu,Danye Zuo,Wei Wang,Jun Ma
DOI: https://doi.org/10.1021/acs.est.1c02687
2021-07-28
Abstract:Membrane distillation (MD) is a promising technology for treating the concentrated seawater discharged from the desalination process. Interconnected porous membranes, fabricated by additive manufacturing, have received significant attention for MD technology because of their excellent permeability. However, their poor hydrophobic durability induced by the deformation of pores constrains their water desalination performance. Herein, an in situ three-dimensional (3D) welding approach involving emulsion electrospinning is reported for fabricating robust nanofibrous membranes. The reported method is simple and effective for welding nanofibers at their intersections, and the reinforced membrane pores are uniform in the 3D space. The results show that the in situ 3D welded nanofibrous membrane, with a stability of 170 h and water recovery of 76.9%, exhibits better desalination performance than the nonwelded (superhydrophobic) nanofibrous membrane and the postwelded (superhydrophobic) nanofibrous membrane. Furthermore, the stability mechanism of the in situ 3D welded nanofibrous membrane and the two different wetting mechanisms of the nonwelded and postwelded nanofibrous membranes were investigated in the current work. More significantly, the in situ 3D welded nanofibrous membrane can further concentrate the actual concentrated seawater (121°E, 37°N) to crystallization, demonstrating its potential applications for the desalination of challenging concentrated seawater.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.est.1c02687.Electrospinning parameters (Method S1), modification methods (Method S2), salt rejection (Method S3), SEM–EDS elemental percentage (Method S4), LEP (Method S5), Owens–Wendt method (Method S6), tensile test (Method S7), abrasion test and peel test (Method S8), Antoine equation (Method S9), dispersive component and polar component (Table S1), seawater quality (Table S2), MD performance of different membranes (Table S3), Schematic diagram of the LEP device (Figure S1), schematic diagrams of the DCMD system (Figure S2), relationship between conductivity and NaCl concentration (Figure S3), mixture of immiscible n-hexane and DMF (Figure S4), SEM–EDS elemental percentage (Figure S5), SEM–EDS elemental maps (Figure S6), SEM image of the postwelded membrane (Figure S7), abrasion test (Figure S8), peel test (Figure S9), SEM image of the membrane after running (Figure S10), photograph of the postwelded membrane (Figure S11), cross-section SEM images of the postwelded membrane (Figure S12), photographs of the nonwelded and postwelded superhydrophobic nanofibrous membranes (Figure S13), and water flux and distillate conductivity trend (Figure S14) (PDF)This article has not yet been cited by other publications.
environmental sciences,engineering, environmental