Improving the hydrophobicity and mechanical properties of starch nanofibrous films by electrospinning and cross-linking for food packaging applications

Weijia Zhu,Die Zhang,Xiaoqing Liu,Tiezheng Ma,Jiangling He,Qi Dong,Zia-ud Din,Jiaojiao Zhou,Lei Chen,Zhongze Hu,Jie Cai

DOI: https://doi.org/10.1016/j.lwt.2022.114005

2022-01-01

Abstract:Many efforts have been devoted to developing starch-based films as an alternative to non-degradable petroleum -based plastic food packaging. However, the application of starch-based films still faces serious challenges due to their water sensitivity and poor mechanical properties. In this work, a simple route was proposed to develop crosslinked starch nanofibrous films (C-SNFs) through electrospinning of starch solution, followed by cross -linking in glutaraldehyde (GTA) vapor. The effect of electrospinning parameters such as starch concentration (20-30 wt%), applied voltage (15-25 kV), and collecting distance (10-20 cm) on fiber morphology was studied. Compared with solution-cast starch films, electrospun starch nanofibrous films (SNFs) showed superior flexibility but poor mechanical strength and water sensitivity. After GTA crosslinking post-treatment, the tensile strength and water contact angle (WCA) of SNFs could be enhanced up to-9.65 MPa and-94.3 degrees, respectively. Results from this work could provide a facile route to fabricate starch-based film materials that showed a promising potential application in the food packaging field.