Effect of Ru on microstructure evolution of the fourth generation nickel-based single crystal superalloy DD22 during long-term aging br

Zhao Yunsong,Yang Zhao,Chen Ruizhi,Zhang Jian,Luo Yushi,Liu Lirong

DOI: https://doi.org/10.11868/j.issn.1001-4381.2022.000105

2022-01-01

Journal of Materials Engineering

Abstract:The morphological evolution of Y phase, the precipitation of TCP phases and the evolution of the interfacial dislocation networks in DD22 nickel-based single crystal superalloys with different Ru contents (3% and 5%, mass fraction) were investigated by transmission electron microscopy and field emission scanning electron microscopy during long-term aging at 1130 degrees C. The results show that y phase of 5Ru alloy are smaller in size and more regular in shape than that of 3Ru alloy. The mismatch of Y/Y ' phases is larger in 5Ru alloy, and the high content of Ru causes the reverse distribution of elements such as Re and Mo. During long-term aging at 1130 degrees C, the coarsening rate, dissolution rate and rafting rate of y ' phase in 5Ru alloy are lower than those of 3Ru alloy. There is still no TCP phase precipitation in 5Ru alloy after long-term aging for 1000 h, while a small amount of TCP phase is precipitated in 3Ru alloy after long-term aging for 50 h. With the prolongation of long-term aging time, the number and size of TCP phases both increase. Compared with 3Ru alloy, the interfacial dislocation networks of 5Ru alloy are denser and more regular after long-term aging for 1000 h. Above all, the reverse distribution of elements and low diffusion coefficient of Ru make 5Ru alloy exhibit higher microstructural stability than 3Ru alloy.