Fast-pyrolysis Lignin-Biochar As an Excellent Precursor for High-Performance Capacitors

Lingyan Zhu,Xudong Liu,Yuan Wu,Qifan Wang,Haotian Wang,Dongbing Li

DOI: https://doi.org/10.1016/j.renene.2022.08.115

IF: 8.7

2022-01-01

Renewable Energy

Abstract:Lignin-based activated carbons (LAC) were produced using thermochemical pretreatment and chemical activa-tion with KOH. Fast pyrolysis at 550 C in a CO2/N2 atmosphere resulted in lignin char (LC) with a more developed porous structure than slow pyrolysis. The effect of activation conditions (KOH usage, temperature, and duration) on surface/physicochemical properties and electrochemical characteristics of the resulting LAC was fully studied. Using fast pyrolysis lignin char as a precursor and optimized activation conditions (wKOH:wLC = 2, 800 C, and 2 h), the resulting LAC featured a large surface area of 2149.5 m2 g-1, a total pore volume of 0.88 m3 g- 1 supercapacitor could offer superior energy density (19.15 W h kg-1 at 250 W kg-1 power density) and a stable lifetime (98.2% of original capacity after 10,000 charge-discharge cycles). The excellent capacitor performance of LAC was attributed to its microporous-mesoporous structure developed from fast pyrolysis and subsequent chemical activation. , and high capacitance of 300 F g-1 at 0.5 A g-1 in a 6 mol L-1 KOH electrolyte. The LAC-based symmetric