The Effects of Adding Molybdenum Tailings As Cementitious Paste Replacement on the Fluidity, Mechanical Properties and Micro-Structure of Concrete

Tao Luo,Yu Yi,Qiang Sun,Leo Gu Li,Liyun Tang,Cheng Hua
DOI: https://doi.org/10.1016/j.jobe.2022.105377
IF: 7.144
2022-01-01
Journal of Building Engineering
Abstract:To reduce the land occupation and environmental pollution caused by the accumulation of molybdenum tailings (MT), MT has been used as cement or fine aggregate replacement to pro-duce concrete. Molybdenum tailings concrete (MTC) was prepared by replacing cement paste with MT of equal mass in this study in order to offer one more option for the adding of MT into concrete. The workability of the concrete mixture and the mechanical properties of the hardened concrete were investigated. The internal pore structure characteristics and micro-morphology of MTC were analyzed by nuclear magnetic resonance (NMR) and scanning electron microscopy (SEM), respectively. The results showed that, as the MT replacement rate increases, the slump of the concrete mixture decreases, the air content increases firstly and then decreases, the compres-sive strength and splitting tensile strength decreases firstly and then increase with the optimum MT replacement rate at 10%; the total porosity of concrete increases and then decreases, both the compressive strength and splitting tensile strength are inversely proportional to the porosity. When the MT replacement rate is 7.5% and 10%, the number of medium capillary pores (0-100 nm) decreases significantly, while the number of capillary pores (100-1000 nm) and air pores (>1000 nm) gradually increases.
What problem does this paper attempt to address?