Abstract:A novel biosorbent PEI-HOCM was successfully prepared by grafting polyethyleneimine (PEI) onto H2O2-oxidized cellulose membrane (HOCM). The whole systhesis process occurred in aqueous solution and was environmentally friendly without any toxic cross-linkers involved. ATR-FTIR, XPS and titration analysis confirmed that the hydroxyl groups of cellulose were oxidized to carbonyl groups by H2O2 and PEI was successfully introduced to the HOCM. The PEI-HOCM had positively charged surface (+ 20.6 to + 86.6 mV) at the measured pH range 3–9 according to the zeta potential analysis. The adsorption of Cr(VI) on the PEI-HOCM obeyed the pseudo-second-order kinetic model and Langmuir isotherm model. Its maximum equilibrium adsorption capacity was 147.06 mg/g at 25 °C, which was much higher than that of cellulose membrane (CM, 30.61 mg/g). According to the obtained results from the intraparticle diffusion, Body kinetic and diffusion-chemisorption models, film diffusion was the rate-limiting step and chemical adsorption was the main mechanism of Cr(VI) adsorption. The Cr(VI) adsorbed on the PEI-HOCM was completely reduced to Cr(III), suggesting that PEI-HOCM was not only useful for Cr(VI) removal but also good for its detoxification. The competitive uptakes from coexisting components (Na+, Mg2+, Ca2+, phenol, Cl− and NO3−) were insignificant except H2PO4− and SO42− which reduced the Cr(VI) uptake with a efficiency loss of 22–41%. Ionic strength had little effect on the adsorption in the range of 0–1000 mg/L NaCl. After five adsorption/desorption cycles, the PEI-HOCM still retained good adsorption capacity. More importantly, it can be separated easily after adsorption, which will greatly benefit the wastewater treatment by simplifying the separation procedure and reducing costs.Graphical abstract

Tannin-coated PVA/PVP/PEI nanofibrous membrane as a highly effective adsorbent and detoxifier for Cr(VI) contamination in water

Negatively-charged Nanofiltration Membrane and Its Hexavalent Chromium Removal Performance.

The Efficient Removal of Low Concentration Hexavalent Chromium Via Combining Charged Microporous Membrane and Micellar Adsorption Filtration

Ultra-high capacity and anti-interference for Cr(VI) removal by tannin-polyvinylimine modified graphite carbon nitride

Chromate Removal by Electrospun PVA/PEI Nanofibers: Adsorption, Reduction, and Effects of Co-Existing Ions

Polyvinylamine-grafted polypropylene membranes for adsorptive removal of Cr(VI) from water

Polydopamine-assisted polyethyleneimine grafting on electrospun cellulose acetate/TiO 2 fibers towards highly efficient removal of Cr(VI)

Novel montmorillonite/jute composites functionalized with polyethyleneimine and cetyltrimethylammonium bromide for Cr(VI) adsorption

Flexible and free-standing pristine polypyrrole membranes with a nanotube structure for repeatable Cr(VI) ion removal

Thiourea crosslinked-amino modified graphene nanoflakes as an effective adsorbent to confine Cr(VI) via multiple combination mechanisms

Facile Synthesis of Polyethylene Glycol@Tannin-Amine Microsphere towards Cr(VI) Removal

Integration of adsorption, reduction, and filtration in PANI/PVDF nanofiber composite membrane for removal of Cr(VI)

Facile synthesis of ZIF-8 incorporated electrospun PAN/PEI nanofibrous composite membrane for efficient Cr(VI) adsorption from water

Recyclable adsorption removal and fluorescent monitoring of hexavalent chromium by electrospun nanofibers membrane derived from Tb 3+ coordinating polyarylene ether amidoxime

Amine-functionalized cellulose nanofiber-sodium alginate-Fe(III) porous hollow beads for the efficient removal of Cr(VI)

Facile synthesis of poly(tannic acid-1,4-butanediamine) microsphere based on the "self-assembly to polymerization" mechanism and its fast removal feature toward Cr(VI) ions

One-Step Preparation of PVDF/GO Electrospun Nanofibrous Membrane for High-Efficient Adsorption of Cr(VI)

Synthesis of Novel Aminated Cellulose Microsphere Adsorbent for Efficient Cr(VI) Removal

In-Depth Sulfhydryl-Modified Cellulose Fibers for Efficient and Rapid Adsorption of Cr(VI)

Electrically Controlled Adsorptive Membranes with Tunable Affinity for Selective Chromium (VI) Separation from Water.

Polyethylenimine grafted H2O2-oxidized cellulose membrane as a novel biosorbent for Cr(VI) adsorption and detoxification from aqueous solution