Abstract:A series of dealuminated mordenite (MOR) samples with different acidities and various porosities were prepared through steam treatment of H+/Na+ mordenite. The obtained zeolites were elaborately characterized by X-ray diffraction, N-2 adsorption-desorption, scanning electron microscopy, Si-29 nuclear magnetic resonance (NMR), Al-27 NMR, NH3 temperature-programmed desorption, and Fourier transform infrared spectroscopy, and the catalytic performance for dimethyl ether (DME) carbonylation was investigated. The characterization results revealed that the kind of cation balancing the zeolite charge had a great effect on the crystalline structure and acidity of mordenite zeolite during steam treatment and ion-exchange processes. Dealumination was observed both on Na-MOR and H-MOR, but it was much milder on the Na-MOR zeolite comparatively. After Na-MOR was treated with steam, its structure was well-preserved, but side pockets of mordenite were opened, resulting in an increased microporous volume and strong acid sites. Interestingly, it was found that the removal of framework Al in the 12MR channel was favored over the 8MR channel during steaming of Na-MOR, leading to the mordenite to possess more acid sites in the 8MR channel compared with those in the 12MR channel. As for the steamed H-MOR, both the crystalline structure and porosity were obviously damaged, resulting in a decreased microporous volume and acidity. The influence was more significant in the 8MR channel of H-MOR due to the obvious removal of framework Al and blockage of side pockets. The performance tests revealed that Na-MOR treated with steam was an effective way to enhance the catalytic performance for DME carbonylation reaction. The N-773 catalyst (steamed with Na-MOR at 773 K) showed a methyl acetate product rate of 0.33 gg(-1) h(-1), which was much higher than that of the parent H-MOR (0.23 gg(-1) h(-1)). Moreover, the dealuminated catalyst exhibited a slow deactivation rate, which was possibly ascribed to the reduced strong acid sites in the 12MR channels. Although the steam treatment of H-MOR resulted in a lower activity in the DME carbonylation reaction, it exhibited a higher MeOAc selectivity and improved stability for its overall decreased acidity.

Preparation of shaped binderless mordenite catalysts with controllable crystal sizes and their carbonylation performance

Synthesis of Nanocrystalline Mordenite Zeolite with Improved Performance in Benzene Alkylation and N‐paraffins Hydroconversion

Wheel-like Mordenite Nanoassemblies with Shortened Channel Lengths for Improved Catalytic Performance in Dimethyl Ether Carbonylation

PREPARATION AND PROPERTIES OF A NEW KIND OF ACID CATALYST OF ZEOLITE COATING ON METAL-SURFACE

Improved Catalytic Performance in Dimethyl Ether Carbonylation over Hierarchical Mordenite by Enhancing Mass Transfer

An efficient synthesis strategy for MOR zeolite

Facile synthesis of mordenite zeolites from bamboo leaves ash for acetalization of benzaldehye and glycerol using non-microwave instant heating

Synthesis of Hierarchical Porous H-mordenite Zeolite for Carbonylation of Dimethyl Ether

Impact of Various Silicon Sources on the Synthesis of Mordenite and Differences in the Carbonylation Reaction of Dimethyl Ether

Effect of Steam Treatment on the Properties of Mordenite and Its Catalytic Performance in a DME Carbonylation Reaction

Synthesis of Ultra-Small Mordenite Zeolite Nanoparticles

High Ethylene Selectivity in Methanol‐to‐Olefin (MTO) Reaction over MOR‐Zeolite Nanosheets

Influence of Pseudo-Boehmite Binder Modified Dealuminated Mordenite on Friedel–Crafts Alkylation

Nanocrystalline sodium mordenite as an efficient low-concentration CO 2 adsorbent

Zeolite Nanocrystals (MOR, EU-1, and ZSM-12) Synthesized Using a Versatile Diquaternary Ammonium Template as Robust Catalysts

Efficient synthesis of high-silica SSZ-13 zeolite and its catalytic performance in MTO reaction

Synthesis and Catalytic Performances of MOR/BEA Core-Shell Composite-Zeolites

Selective conversion of methanol to propylene over highly dealuminated mordenite: Al location and crystal morphology effects

A Study into the γ-Al2O3 Binder Influence on Nano-H-ZSM-5 via Scaled-Up Laboratory Methanol-to-Hydrocarbon Reaction

Competition balance between mesoporous self-assembly and crystallization of zeolite: A key to the formation of mesoporous zeolite

Mordenite Nanorods and Nanosheets Prepared in Presence of Gemini Type Surfactants