Abstract:In this work, 70 vol% TiC/Al cermets with the addition of 5 vol% Ta, Nb and Zr elements were successfully fabricated by combustion synthesis and hot-pressing method. Among them, Ta, Nb and Zr elements generated (Ti, X)C (X = Ta, Nb and Zr) solid solutions and Al3X (X = Ta, Nb and Zr) intermediate phases during the reaction process, and refine TiC particles significantly. Especially, Ta and Nb elements decreased the crystallographic mismatch of the Al/TiC interface. The addition of Ta improves the compression properties of TiC/Al cermets at room temperature and high temperature. The addition of Nb and Zr impairs the room temperature compress-ibility of the TiC/Al cermet, but improves the high temperature (300 degrees C) compressibility. The strengthening mechanisms of TiC/Al cermets after adding Ta, Nb and Zr were mainly solid solution strengthening, grain refinement strengthening and the reduction of lattice mismatch at the Al/TiC interface. The reduced mechanical properties of TiC/Al cermets at room temperature after the addition of Nb and Zr elements were due to the presence of intermediate phases.

Effect of Ta, Nb and Zr Additions on the Microstructures and Mechanical Properties of 70 Vol% TiC/Al Cermets