The Superior Properties of Spark Plasma Sintered La-Fe-Si Magnetocaloric Alloys

Yu-Cai Wu,Yuan-Xin Li,Xi -Chun Zhong,Cui-Lan Liu,Jiao-Hong Huang,Hong-Ya Yu,Zhong-Wu Liu,Ming -Long Zhong,Zhen-Chen Zhong,Raju V. Ramanujan

DOI: https://doi.org/10.1016/j.materresbull.2022.111974

IF: 5.6

2022-01-01

Materials Research Bulletin

Abstract:LaFe(11.8)Si(1.2 )bulk magnetocaloric materials were prepared by hot-pressing sintering (HPS) and spark plasma sintering (SPS) techniques. The effects of the particle size, phase content and porosity on the thermal conductivity, mechanical and magnetocaloric properties were studied. Our results demonstrated that the reduction of porosity in bulk magnetocaloric materials was an effective way to enhance the magnetocaloric effect. Compared to the HPS samples, the porosity of the SPS samples, with an initial powder size of 100-200 mu m, reduced by 18%, which resulted in (-delta S-M)(max )and (-delta S-M)(V)(max) increasing by 15% and 19%, respectively. The SPS samples had a large (-delta S-M)(max) value in the range of 7.3-12.8 J/kg.K (mu(0)AH=2T), good maximum compressive strength of 216-636 MPa and thermal conductivity of 5.8-7.6 W/m.K. Thus, SPS has been shown to be a promising pro-cessing technology to fabricate magnetocaloric materials (MCMs) with excellent performance.