Abstract:To enhance the specific strength of cubic lattice structure, three design strategies are applied: substituting solid struts with hollow ones, increasing the material proportion of vertical struts, and introducing cross plates into the hollow struts. The specific yield compressive strength of the optimized lattice structure reaches up to 230 MPa cm3 g−1, significantly surpassing that of the TC4 matrix. Additive manufacturing permits the precision design and meticulous fabrication of lattice structures, thereby unlocking their potential performance capabilities. Herein, to enhance the specific strength of the cubic lattice structure, three design strategies are applied: substituting solid struts with hollow ones, increasing the material proportion of vertical struts, and introducing cross plates into the hollow struts. The results demonstrate that the strategy of substituting solid struts with hollow ones effectively contributes to a substantial enhancement of 113% in the compressive yield strength of lattice structures. Furthermore, increasing the vertical material proportion from 70% to 85% while maintaining a constant relative density of 0.30, a significant enhancement is observed in both yield and ultimate strength. Additionally, introducing cross plates into the hollow struts at a vertical material proportion of 90% results in a remarkable enhancement of the specific yield strength to 230 MPa cm3 g−1, significantly surpassing that of the TC4 matrix. The optimized lattice structures exhibit exceptional uniaxial strength, tremendously exceeding the predicted limits of the Gibson–Ashby model. Thus, the Gibson–Ashby model is modified by considering the vertical material proportion Cv. These findings are expected to establish a foundational framework for the optimizing of anisotropic lattice structures by remarkably enhancing their specific strength.

Mechanical Properties and Failure Modes of Additively Manufactured Ti6Al4V Lattice Structures under Quasi-Static Compressive Loading

Fracture and Failure Behavior of Additive Manufactured Ti6Al4V Lattice Structures under Compressive Load

Quasi-static Compressive Behaviors of Large-Size Titanium Lattice Sandwich Structure Based on Pulse Hot-Wire Arc Additive Manufacturing

Heterogeneous compressive responses of additively manufactured Ti-6Al-4V lattice structures by varying geometric parameters of cells

Mechanical characterization of additively-manufactured metallic lattice structures with hollow struts under static and dynamic loadings

Mechanical properties of additively manufactured variable lattice structures of Ti6Al4V

Additive manufacturing of Ti-6Al-4V lattice structures with high structural integrity under large compressive deformation

A Study on the Compressive Behavior of Additively Manufactured AlSi10Mg Lattice Structures

Compressive Behavior of Novel Additively Manufactured Ti-6Al-4V Lattice Structures: Experimental and Numerical Studies

Compressive properties of imperfect Ti-6Al-4V lattice structure fabricated by electron beam powder bed fusion under static and dynamic loadings

Fracture Characteristic Analysis of Cellular Lattice Structures under Tensile Load

Effect of geometric defects on the mechanical properties of additive manufactured Ti6Al4V lattice structures

Mechanical Behaviors of SLM Additive Manufactured Octet-Truss and Truncated-Octahedron Lattice Structures with Uniform and Taper Beams

Compression Experiment and Failure Analysis of Additive Manufactured Multi-Layer Lattice Sandwich Structure

Additively-manufactured Functionally Graded Ti-6Al-4V Lattice Structures with High Strength under Static and Dynamic Loading: Experiments

Quasi-static Analysis of Mechanical Properties of Ti6Al4V Lattice Structures Manufactured Using Selective Laser Melting

Generative design and mechanical properties of the lattice structures for tensile and compressive loading conditions fabricated by selective laser melting

Additive Manufacturing of Anisotropic TC4 Cubic Hollow‐Strut Lattice Structures with High Specific Yield Strength: Optimization, Properties, and Failure Modes

Compressive Properties and Micro-Structural Characteristics of Ti–6Al–4V Fabricated by Electron Beam Melting and Selective Laser Melting

Influence of Bracing on the Mechanical Properties of Ti6Al4V Lattice Structures

Mechanical Properties Evaluation Based on the Variable Gradient of Body-Centered-Cubic-Based Lattice Structure Prepared by Laser Powder Bed Fusion