Abstract:The aim of this study was to investigate the influence of fineness and heat-treatment on the pozzolanic and engineering properties of volcanic ash. To this end, two different fineness levels of volcanic ash, ultra-fine (VAF) and fine (VA), without and after heat treatment at different temperatures (VA550, VA650, and VA750), were partially substituted for cement. In addition to the control (100% cement), five binary mortar mixes, each containing 20% of the different types of volcanic ash (VAF and VA; heat-treated and not), were prepared. First, X-ray fluorescence (XRF), X-ray powder diffraction (XRD), particle size analysis, and modified Chappelle tests were used to characterize the material. All mortar mixes were then tested for compressive strength development, water absorption, and apparent porosity. Finally, the microstructure of each of the mixes was evaluated by performing XRD, thermogravimetric analysis (TGA), and Fourier transform infrared spectroscopy (FTIR) analyses on paste samples at 91 days post-formation. The XRD and Chappelle reactivity results revealed increased pozzolanic reactivity with increasing volcanic ash fineness. In contrast, heat treatment adversely affected the pozzolanic reactivity of the volcanic ash due to the formation of crystalline phases at high temperatures. The mortars containing VAF20 (VAF, no heat, at 20%) showed slightly improved compressive strength (69.6 MPa) than the control (68.1 MPa) and all other binary mixes (66.7, 63.5, 64.2, and 63.9 MPa for VA20, VA20-550, VA20-650, and VA20-750, respectively) at 91 days. The mortar containing VAF20 demonstrated the lowest level of water absorption (9.3%) and apparent porosity (19.1%) of all mixes, including the control. The XRD results for the paste samples show that both VA and VAF showed the least intensity of portlandite phase, as compared to the control and other binary mixes. TGA results also show that binary mixes of VA and VAF have a reduced amount of portlandite, resulting in the densification of the mixes’ microstructures. With the addition of VAF, there is a significant shift in the FTIR band from 980 to 992 cm−1, which causes the formation of additional C–S–H gels that lead to the densification of the paste matrix. These results demonstrate that VAF exhibits high pozzolanic reactivity, making it suitable for use as a natural pozzolan that can partially substitute cement in the production of strong, durable, and environmentally friendly concrete.

Assessment of select direct and indirect pozzolanic reactivity test outcomes with robust regression and ranking analysis

Comprehensive Review of Direct and Indirect Pozzolanic Reactivity Testing Methods

Eco-Pozzolans as Raw Material for Sustainable Construction Industry: Comparative Evaluation of Reactivity Through Direct and Indirect Methods

Experimental Investigation on Reactive Powder Concrete by Partial Replacement of Cement with Different Pozzolanic Materials

A comprehensive experimental study on the performance of pumice powder in self-compacting concrete (SCC)

Analysis of chemical-mineralogical content of brick waste as a pozzolan substitute material in blended cement

Sustainable and Durable Performance of Pozzolanic Additions to Prevent Alkali-Silica Reaction (ASR) Promoted by Aggregates with Different Reaction Rates

Kinetic and Thermodynamic Study in Pozzolanic Chemical Systems as an Alternative for Chapelle Test

Estimation of non-traditional supplementary cementitious materials potential to prevent alkali-silica reaction using pozzolanic reactivity and bulk resistivity

Effect of Fineness and Heat Treatment on the Pozzolanic Activity of Natural Volcanic Ash for Its Utilization as Supplementary Cementitious Materials

Determination of the Pozzolanic Activities of Trachyte and Rhyolite and Comparison of the Test Methods Implemented

Pozzolanic Reactivity of High-Alkali Supplementary Cementitious Materials and Its Impact on Mitigation of Alkali-Silica Reaction

Evaluation on Reactivity of Fly Ash from Different Sources in Alkali Activated System-Progressing Environmentally Construction Through Waste Utilization

Effect of Fineness of Basaltic Volcanic Ash on Pozzolanic Reactivity, ASR Expansion and Drying Shrinkage of Blended Cement Mortars

Revealing the connection between carbonation regimes and early pozzolanic reactivity of recycled concrete powder: Impact of composition and microstructure

Divergence between Performance in the Field and Laboratory Test Results for Alkali-Silica Reaction

Cost-effective and green additives of pozzolanic material derived from the waste of alum sludge for successful replacement of portland cement

Effect of volcanic pumice powder ash on the properties of cement concrete using response surface methodology

Influence of Pozzolan, Slag and Recycled Aggregates on the Mechanical and Durability Properties of Low Cement Concrete

EFFECT OF TEMPERATURE ON THE HYDRATION OF ORDINARY PORTLAND CEMENT AND THE POZZOLANIC REACTION OF VOLCANIC GLASS POWDER

Mechanical properties of sustainable reactive powder concrete made with low cement content and high amount of fly ash and silica fume