Atomic-Dispersed Coordinated Unsaturated Nickel–Nitrogen Sites in Hollow Carbon Spheres for the Efficient Electrochemical CO 2 Reduction
Pengfei Yao,Jiangwei Zhang,Yanling Qiu,Qiong Zheng,Huamin Zhang,Jingwang Yan,Xianfeng Li
DOI: https://doi.org/10.1021/acssuschemeng.1c00743
2021-04-06
Abstract:Reducing carbon dioxide to high value-added chemicals is of high importance due to its vital role in mitigating CO<sub>2</sub> emission and energy crisis. However, seeking for robust catalysts with low overpotential, high selectivity, and stability is extremely challenging. Herein, a single Ni atom anchored on an N-doped carbon (Ni–N–C) catalyst was designed and prepared via a facile synthesis method to embed highly and evenly dispersed, coordinated unsaturated nickel–nitrogen active sites into a hollow carbon matrix with abundant micropores. The prepared Ni–N–C catalysts possess a unique electronic structure, coordination environment, and maximized atomic utilization, which accordingly show a higher intrinsic activity and remarkable selectivity for the electrochemical reduction of CO<sub>2</sub>. Additionally, the coordination structure and content of Ni can be easily modulated by changing the calcination temperature, which plays a vital role for the catalytical performance. As a result, the Ni–N–C catalysts achieve over 90% for CO at a wide potential window from −0.6 to −1.0 V with a maximum value of 97% at −0.8 V. This paper paves a facile way to develop high-performance single atomic catalysts with a tunable Ni–N coordination structure for CO<sub>2</sub> reduction.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c00743?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c00743</a>.TEM, SEM images, XPS spectra, Raman spectra, XRD, BET, and FEs of N-HCS-1000, Ni/N-HCS-T, and HCS-N-T-Ni-HCS-1000; SEM and TEM images of HCS-600; nitrogen adsorption–desorption isotherm of HCS-600, Ni/N-HCS-1000, and HCS-N-T-Ni-HCS-1000; pore size distributions of HCS-600, Ni/N-HCS-T, and N-HCS-1000; STEM images of Ni/N-HCS-1000; TG-MS for Ni/N-HCS-800; LSV curves of all samples; summary of N content for Ni/N-HCS-T and N-HCS-1000; surface area for the materials; and comparison of electrocatalytic performance over Ni/N-HCS-1000 with other reported single-atom catalysts (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c00743/suppl_file/sc1c00743_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology