Abstract:The interlayer expanded zeolite COE-4 was synthesized using silylation agents such as dichlorodimethylsilane (DCDMS) as layer linlcer from layered silicate RUB-36 precursor. Solid-state NMR techniques combined with theoretical calculations have proven to be a useful characterization method to investigate the structure and porosity of the interlayer expanded zeolites. XRD and Si-29 MAS NMR results show that after calcination the layer spacing of COE-4 is enlarged by 2.6 angstrom compared with that of RUB-37, indicating that pore windows between the layers are enlarged from 8-membered ring (8-MR) pores to 10-MR pores due to the formation of Si(OH)(2) pillar between adjacent layers. Hyperpolarized (HP) Xe-129 NMR results indicate that after interlayer expansion, Xe atoms can be adsorbed in the 10-MR channels of COE-4, and the 10-IVIR channels are homogeneously distributed like ZSM-5. For COE-4, Xe has a stronger interaction with the channel walls containing dual silanol groups. H-1 MAS NMR combined with theoretical calculations malce a clear assignment of dual silanol groups at 3.3 ppm, and the concentration of dual silanols is 2.2 mmol/g, which is 1-2 orders of magnitude larger than the concentration of the other two types of existing isolated and hydrogen-bonded silanol groups. After introduction of pyridine-d(5), one Si-OH from the dual silanol groups has a weak hydrogen bond interaction with pyridine molecule, and the adsorbed pyridine molecule may experience chemical exchange with the other Si-OH of the dual silanol group and therefore H-1 NMR signal of dual silanol groups shows a weak broad peak at 5.7 ppm after pyridine adsorption.

Synthesis and Interlayer Structure Reconstruction of a New Layered Zeolitic Aluminosilicate

Preparation of Interlayer-Expanded Zeolite from Lamellar Precursor Nu-6(1) by Silylation

The preparation of an elastomer/silicate layer nanocompound with an exfoliated structure and a strong ionic interfacial interaction by utilizing an elastomer latex containing pyridine groups.

Structural Investigation of Interlayer-Expanded Zeolite by Hyperpolarized 129xe and 1H NMR Spectroscopy

Interlayer expansion of the layered zeolite precursor RUB-39: A universal method to synthesize functionalized microporous silicates

Synthesis of Extra-Large-Pore Zeolite ECNU-9 with Intersecting 14*12-Ring Channels

Designable Synthesis of Layered Silicates and Tunable Interlayer Expanded to Zeolites.

Synthesis of Large‐Pore ECNU‐19 Material (12 × 8‐R) Via Interlayer‐Expansion of HUS‐2 Lamellar Silicate

Methodology for synthesizing crystalline metallosilicates with expanded pore windows through molecular alkoxysilylation of zeolitic lamellar precursors.

Synthesis and characterization of a layered aluminosilicate NUD-11 and its transformation to a 3D stable zeolite

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Structural Characterization of Interlayer Expanded Zeolite Prepared from Ferrierite Lamellar Precursor

Synthesis, Characterization, and Catalytic Properties of Interlayer Expanded Aluminosilicate IEZ-PLS-3

Topotactic Conversion of Alkali-Treated Intergrown Germanosilicate CIT-13 into Single-Crystalline ECNU-21 Zeolite As Shape-Selective Catalyst for Ethylene Oxide Hydration.

Syntheses, Structure Solutions, and Catalytic Performance of Two Novel Layered Silicates

A New Layered Silicogermanate PKU-23 and Its Transformation to a Zeolite with Three-Dimensional Channels

A New Zeolite Formed from Interlayer Expansion of the Precursor COK-5

Cooperative Structure-Directing Effects in the Synthesis of a Low-Silica Zeolite Phillipsite Analogue

Two Coexisting Forms of Simple Molecules for Directing Sesqui-Unit-Cell Zeolite Nanosheets

Synthesis of Novel Titanosilicate Catalysts by Simultaneous Isomorphous Substitution and Interlayer Expansion of Zeolitic Layered Silicates

From Layered Zeolite Precursors to Zeolites with a Three-Dimensional Porosity: Textural and Structural Modifications Through Alkaline Treatment