Abstract:Nb-Si base alloys have attracted considerable attentions as the potential high temperature structural materials working in the service temperature range of 1200 similar to 1400 degrees C because of their high melting points (>1750 degrees C), moderate densities (6.6 similar to 7.2 g/cm(3)) and excellent high temperature strength. However, the mismatching between room temperature fracture toughness and high temperature strength has limited their practical applications. Directional solidification (DS) and alloying have been proved to be the effective methods to overcome this critical issue. The DS processes used to prepare Nb-Si base alloys included Czochralski directional solidification in a copper crucible, electron beam directional solidification, optical floating zone melting, integrally directional solidification and electromagnetic cold crucible directional solidification (ECCDS). The previous studies focused on the effect of process parameters on microstructure and mechanical properties in the steady-state growth region (SSGR). However, the microstructure in the SSGR was controlled by the solid-liquid interface, and the solid-liquid interface was controlled by process parameters. Therefore, the study about the effect of process parameters on solid-liquid interface was very important. In this work, the master alloy with the nominal composition of Nb-22Ti-16Si-3Cr-3Al-2Hf (atomic fraction, %) was prepared by vaccum non-consumable arc-melting first, and then induction skull melting. The DS experiments were performed in the ECCDS device equipped with a square water cooled copper crucible (internal dimension; 26 mmx26 mmx120 mm) and a Ga-In alloy pool. There were three processing parameters in ECCDS including heating power of power supply, withdrawal rate and holding time. The DS ingots were prepared according to the orthogonal test (L-9(3(3))). Instability degree was defined as the ratio of the height of solid-liquid interface to the width of the DS ingot. The results showed that there were three macroscopic morphologies of solid-liquid interfaces; the increase of holding time, decrease of withdrawal rate and elevation of heating power were conducive to keeping the solid-liquid interface macroscopic morphology planar. With the increase of withdrawal rate, primary dendrite arm spacing. (d(1)) and secondary dendrite arm spacing (d(2)) decreased gradually; with the increase of heating power, d(1) and d(2) increased gradually; with the increase of holding time, d(1) and d(2) increased first and then decreased. The higher withdrawal rate, lower heating power and less holding time were beneficial to refining the d(1) and d(2).

Morphological Heredity of Intermetallic Nb5Si3 Dendrites in Hypereutectic Nb-Si Based Alloys Via Non-Equilibrium Solidification

Phase-field Simulation of Secondary Dendrite Growth in Directional Solidification of Binary Alloys

Microstructure of the Nb-Si Based Multicomponent Alloy by Electromagnetic Cold Crucible Directional Solidifcation

Formation of Equiaxed Crystal Structures in Directionally Solidified Al-Si Alloys Using Nb-based Heterogeneous Nuclei

Dendritic Si growth morphologies in highly undercooled Al-Si alloys

Morphological Evolution of Primary Β-Nb5si3 Phase in Nb-Mo-Si Alloys

Observation of Dendrite Growth Velocity and Microstructure Transition in Highly Undercooled Single Phase Alloys

Segregation and Morphological Evolution of Si Phase during Electromagnetic Directional Solidification of Hypereutectic Al-Si Alloys

Formation of Near Core-Shell-like Structure and Dual-Phase Nanoprecipitation Behavior in Nb-Si-Ti Based Alloys

The Mechanism of Dendrite Formation in a Solid-State Transformation of High Aluminum Fe-Al Alloys

Mechanism of Solute Hardening and Dislocation Debris-Mediated Ductilization in Nb-Si Alloy

DENDRITE REFINING AND EUTECTIC TRANSFORMATION BEHAVIOR OF NICKEL-BASE SINGLE CRYSTAL (NBSC) SUPERALLOY

Effect of Processing Parameters on Solid-Liquid Interface of Nb-Si Base Alloy Fabricated by Electromagnetic Cold Crucible Directional Solidification

Phase transformation and dislocation behavior dependence on cooling rate in novel refractory high entropy alloy

Effect of Growth Rate on Microstructure and Mechanical Properties in a Directionally Solidified Nb-silicide Base Alloy

Structural, Magnetic, and Mössbauer Study on Nb and Heat Treatment of Fe-Si-B-P-Cu-Nb Ribbons

Solidification microstructure manipulation mechanism of hypoeutectic and hypereutectic Al-Si alloys controlled by trace in-situ nano-Fe 2 B and nano-Fe 3 Si

Investigations on the Solidification Microstructures and Room Temperature Compression Properties of Nb-doped NiAl-32Cr-6Mo Hypereutectic Alloy

Microstructure Evolution and Mechanical Properties of a Directionally Solidified Nb-Ti-Si-Cr-Al-Hf-Dy Alloy

Formation and Crystallization Behavior of Fe-based Amorphous Precursors with Pre-Existing Α-Fe Nanoparticles—structure and Magnetic Properties of High-Cu-content Fe-Si-B-Cu-Nb Nanocrystalline Alloys

Microstructure Evolution in Undercooled Ni-Si Melt