Abstract:Micelles and hydrogels, generally prepared at different concentrations in waters, arouse great interest due to their wide application. However, it is inconvenient and difficult to prepare the micelles and hydrogels at the same concentrations. In this work, different states of a same copolymer, such as micelle solutions and hydrogels, are prepared via the polymerization of the pre-assembled acrylic acid and styrene with the same monomer compositions at the same concentrations. The influence of initiator (azodiisobutyronitrile) concentration on the structures of the aggregates is investigated, and the corresponding molecular structures of the copolymers are studied by nuclear magnetic resonance and dynamic thermomechanical analysis, whereas the morphology of the aggregates is characterized by scanning electron microscope and transmission electron microscope. As a supplement to the experiment, dissipative particle dynamics simulation is further performed to reveal the aggregate structures and the corresponding molecular structures of the copolymers. It is found that, under the same concentration of acrylic acid and styrene, the system with a higher initiator concentration (7.0 x 10(-3) mol/L) tend to form stable spherical micelles of 50 nm diameter, in which the copolymers have longer blocks; while that with a lower initiator concentrations (such as 7.0 x mol/L) tend to form network hydrogels, in which the copolymers have alternated and shorter blocks. Both the dynamic thermomechanical analysis and the simulation results demonstrate that the diblock copolymers and multiblock copolymers are synthesized at the higher and the lower initiator concentration. The different aggregate structures are originated from the different molecular structures. In addition, rheological characterization techniques are employed to investigate the rheological properties of the solutions and the hydrogels to clarify the relations between the properties and the molecular/aggregate structures. The rheological characterization showed the shear thinning non-Newtonian behaviour for both the micelle solutions and the hydrogels, and the gel-point of hydrogels was determined to be at the concentration of 22 wt%. It is found that the hydrogels are recoverable after destruction by large amplitude oscillatory shear. The work can serve as an example to clarify the role of the polymer microstructure in determining the material properties and to provide guides for constructing materials with the similar composition but different aggregate structure.

Lightly Cross-Linked Microgels by Precipitation Polymerization of Maleic Anhydride and Styrenic Monomers

Micron-Size Functional Uniform Pmma Particles by Dispersion Copolymerization in Polar Media

Micron-Size Uniform Poly(Methyl Methacrylate) Particles by Dispersion Polymerization in Polar Media 1. Particle Size and Particle Size Distribution

Polyurethane Acrylate Microgel Synthesized by Emulsion Polymerization Using Unsaturated Self-Emulsified Polymer

Preparation of Cross-Linked Microparticles of Poly(glycidyl Methacrylate) by Dispersion Polymerization of Glycidyl Methacrylate Using a PDMS Macromonomer As Stabilizer in Supercritical Carbon Dioxide

Preparation of Micelles and Gels Via Polymerization of Pre-Assembled Styrene and Polyacrylic Acid

Thermo-sensitive ionic microgels via post quaternization cross-linking: fabrication, property, and potential application

Thermosensitive ionic microgels via surfactant-free emulsion copolymerization and in situ quaternization cross-linking.

Formation of Microgels by Utilizing the Reactivity of Catechols with Radicals

Preparation and Characterization of Poly (N-Isopropylacrylamide-co-dimethylaminoethyl Methacrylate) Microgel Latexes

Degradable and Thermosensitive Microgels Synthesized Via Simultaneous Quaternization and Siloxane Condensation

Structural Evolution of Microgels During Precipitation Polymerization Revealed by Light Scattering and Electrophoresis

Crosslinking Strategies for the Microfluidic Production of Microgels

Preparation of micron-size crosslinked microspheres by dispersion copolymerization of polystyrene/2,2′-oxy-bisethanol diacrylate

Monodisperse Styrene-Maleic Anhydride-Isoprene Terpolymer Microspheres with Tunable Crosslinking Density Prepared by Self-Stabilized Precipitation Polymerization

Preparation of Microsized Crosslinked Microspheres by Dispersion Copolymerization of Polystyrene/polyethylene Glycol 200-Dimethacrylae

Highly crosslinked poly(styrene-<i>co</i>-divinylbenzene) microspheres prepared by precipitation polymerization: Effects of the polymerization parameters on the characteristics of the particles

Synthesis and Properties of Organic-Inorganic Hybrid P(Nipam-Co-Am-Co-Tmspma) Microgels

A Novel, Facile Method for the Preparation of Uniform, Reactive Maleic Anhydride/Vinyl Acetate Copolymer Micro‐ and Nanospheres

Absorbent-Adsorbates: Large Amphiphilic Janus Microgels as Droplet Stabilizers

Stabilizer‐free Dispersion Copolymerization of Maleic Anhydride and Vinyl Acetate. I. Effects of Principal Factors on Microspheres