Abstract:An effective strategy is developed to obtain highly reversible Zn anodes with simultaneous outer Helmholtz plane regulation and Zn surface homogenization, by applying zinc sulfate, copper(II) chloride, and poly(N‐diallyldimethylammonium chloride (PDADMAC–CuCl2–ZnSO4) as the electrolyte. Even Zn deposition is obtained and extremely long cycle life is accomplished for Zn//Zn cells with PDADMAC–CuCl2–ZnSO4 electrolyte. Metallic Zn, a promising anode for aqueous energy storage devices, suffers from uncontrolled dendrite growth and corrosion, leading to a short cycle life and low Coulombic efficiency (CE) in Zn‐based batteries. Herein, a composite electrolyte including zinc sulfate, copper(II) chloride, and poly(N‐diallyldimethylammonium chloride) (PDADMAC), denoted as PDADMAC–CuCl2–ZnSO4, is applied to simultaneously reconstruct the outer Helmholtz plane (OHP) and homogenize the Zn surface for highly reversible Zn anodes. The results of characterization, namely Raman spectroscopy, X‐ray photoelectron spectroscopy, X‐ray diffraction, density functional theory calculations, and electrochemical tests, confirm that the addition of chloride ions promotes the adsorption of PDADMAC on the OHP of the electric double layer and controls the Zn deposition process by regulating the electric field. Simultaneously, in situ Zn surface homogenization is accomplished by the reaction of Cu2+ on the Zn surface. As a result, the highly reversible Zn anode sustains extremely long‐term cycling for 2407 h at 5 mA cm−2 with 5 mAh cm−2 and 1300 h at 10 mA cm−2 with 10 mAh cm−2 in Zn//Zn symmetrical cells. A high average CE of 99.3% is achieved over 430 cycles at 15% depth of discharge.

Highly Active Crystal Planes-Oriented Texture for Reversible High-Performance Zn Metal Batteries

A Homogeneous Plating/stripping Mode with Fine Grains for Highly Reversible Zn Anodes

A Seamless Metal-Organic Framework Interphase with Boosted Zn2+Flux and Deposition Kinetics for Long-Living Rechargeable Zn Batteries

Ordered Planar Plating/stripping Enables Deep Cycling Zinc Metal Batteries

Electrocrystallization Regulation Enabled Stacked Hexagonal Platelet Growth Toward Highly Reversible Zinc Anodes

Assembly of Metal–Organic Chemical Conversion Layers As Ion Sieves along with Exposing Zn(002) Planes for Stable Zn Metal Anode

Helmholtz Plane Reconfiguration Enables Robust Zinc Metal Anode in Aqueous Zinc‐Ion Batteries

Epitaxial Deposition of Zn (002) for Stable Zinc Metal Anodes

Stabilizing Zn Metal Anode by Interfacial Self-Assembled Zincophilic Metal-Organic Complex Conversion Layers

Highly Reversible Zn Anode Enabled by Controllable Formation of Nucleation Sites for Zn-Based Batteries

Outer Helmholtz Plane Regulation and In Situ Zn Surface Reconstruction for Highly Reversible Zn Anodes

Oriented Metal Stripping for Highly Reversible Zinc Anode

Suppressing metal corrosion through identification of optimal crystallographic plane for Zn batteries

Highly enhanced reversibility of a Zn anode by in-situ texturing

Crystal Plane Reconstruction and Thin Protective Coatings Formation for Superior Stable Zn Anodes Cycling 1300 h

In Situ Spontaneous Construction of Zinc Phosphate Coating Layer Toward Highly Reversible Zinc Metal Anodes

Highly Reversible Zn Metal Anodes Realized by Synergistically Enhancing Ion Migration Kinetics and Regulating Surface Energy

Highly reversible zinc metal anode enabled by strong Brønsted acid and hydrophobic interfacial chemistry

Regulating Zn Ion Desolvation and Deposition Chemistry Toward Durable and Fast Rechargeable Zn Metal Batteries

A Zincophilic Ion-Conductive Layer with the Desolvation Effect and Oriented Deposition Behavior Achieving Superior Reversibility of Zn Metal Anodes

Zincophilic Ion-Conductive Layer with Desolvation Effect and Oriented Deposition Behavior Achieving Superior Reversibility of Zn Metal Anode