Anisotropic electromagnetic absorption of the aligned Ti₃C₂T_x MXene/RGO nanocomposite foam

Yuanhao Ning,Minglong Yang,Zongbin Zhao,Xianxian Sun,Shuang Yang,Shasha Wang,Lei Liang,Yuanjing Cheng,Weilong Yin,Ye Yuan,Yibin Li

DOI: https://doi.org/10.1016/j.compscitech.2022.109609

IF: 9.1

2022-01-01

Composites Science and Technology

Abstract:Transition metal carbides/nitrides (MXenes) with superb electrical properties have excellent applications for electromagnetic wave absorption (EMA). Whereas, the three-dimensional (3D) MXene's fabrication assemblies with anisotropic EMA performance are still a challenge as MXene nanosheets have weak gelation capabilities. In this study, graphene oxide was introduced to assist in fabricating the 3D MXene/RGO porous foam through the method of unidirectional freeze casting followed by hydrazine hydrate chemical reduction. Combined with the excellent electrical properties of MXene and RGO, the resultant lightweight (similar to 6 mg/cm(3)) MXene/RGO composite foam (MGF) with a free-standing configuration exhibits anisotropic microwave absorption performance. At the sample thickness of 5 mm, MGF-1/2 shows -26.79 dB minimum reflection loss at 4.39 GHz along the perpendicular direction that relates to the unidirectional freeze casting direction. While along the parallel direction, materials with 3 mm thickness reach the maximum effective bandwidth of 8.34 GHz. The lightweight MXene/RGO nanocomposite foam with anisotropic performance may significantly extend the feasibility of MXenes in EMA.