Microstructure and electrical conductivity of A-site fully stoichiometric Na0.5+xBi0.5−xTiO3−δ with different Na/Bi ratios
Xiyong Chen,Mingxin Zhou,Junzuo Shi,Tianquan Liang,Jie Zeng,Xia Yan,Nengneng luo,Weizhou Li,Yuezhou Wei
DOI: https://doi.org/10.1016/j.ceramint.2019.03.011
IF: 5.532
2019-01-01
Ceramics International
Abstract:The effect of nominal Na/Bi ratio on the microstructure and electrical conductivity of A-site fully stoichiometric sodium bismuth titanates, Na0.5+xBi0.5−xTiO3−δ, was investigated in this study. Bulk samples with x = 0, 0.01, 0.03, 0.05, 0.07, and 0.1 were prepared by conventional solid state reaction method. The as-calcined powders primarily exhibited the perovskite structure, which was identified by X-ray diffraction. Electron microscopic investigation of the sintered samples, however, revealed the presence of secondary phases, the amounts of which were found to increase with increasing Na/Bi ratio. Further elemental analysis by energy dispersive spectroscopy indicated that the secondary phases were mainly composed of sodium titanates with different Na/Ti ratios. The grain bulk and grain boundary conductivities of Na0.5+xBi0.5−xTiO3−δ, measured by two-probe AC electrochemical impedance spectroscopy, significantly increased with increasing Na/Bi ratio when x ≤ 0.03, but remained almost constant at higher x. The synergetic effect of oxygen vacancy creation, grain size reduction, and secondary phase formation on the variation in the conductivity upon increasing the nominal Na/Bi ratio in Na0.5+xBi0.5−xTiO3−δ was discussed.