Wood Carbon Based Single-Atom Catalyst for Rechargeable Zn–Air Batteries
Linxin Zhong,Chengyu Jiang,Mengting Zheng,Xinwen Peng,Tongchao Liu,Shibo Xi,Xiao Chi,Qinghua Zhang,Lin Gu,Shanqing Zhang,Ge Shi,Lei Zhang,Kunze Wu,Zehong Chen,Tingzhen Li,Mouad Dahbi,Jones Alami,Khalil Amine,Jun Lu
DOI: https://doi.org/10.1021/acsenergylett.1c01678
IF: 22
2021-09-21
ACS Energy Letters
Abstract:Low-cost and efficient oxygen reduction reaction (ORR)/oxygen evolution reaction (OER) bifunctional electrocatalysts are vital for the applications of rechargeable Zn–air batteries (ZABs). Given the high catalytic activity of single-atom catalysts (SACs), preparing SACs on a large scale for ZABs is desirable but remains challenging. Herein, in situ formation of single-atom Fe–N–C catalysts on plate wood-based porous carbon is achieved via a facile Lewis acid pretreatment and carbonization process. Lewis acid FeCl3 pretreatment on the cell wall of wood not only produces abundant microchannels but also successfully introduces atomically dispersed Fe–N active species into the hierarchical structure. Such uniformly dispersive SACs on the hierarchical structure enhance the ORR/OER performance and durability. A ZAB using the catalyst in the cathode shows a high power density (70.2 mW cm–2, at quasi solid state) and long-term stability. This work provides a new path for the large-scale preparation of high-performance SACs.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsenergylett.1c01678.Experimental details, photos of batch processing of wood with FeCl3, SEM images of natural wood in the vertical direction, SEM images of FeCl3-wood in the vertical direction, SEM images of N-WPC at various magnifications, SEM images of SAC-FeN-WPC at various magnifications, SEM images of ZnCl2-wood in the vertical direction, BET data, Raman spectra for WPC, N-WPC, and SAC-FeN-WPC, N species and contents of SAC-FeN-WPC and N-WPC, SEM-EDS mapping of SAC-FeN-WPC, aberration-corrected HAADF-STEM images of the SAC-FeN-WPC, high-resolution XPS spectrum of Fe 2p for SAC-FeN-WPC, wavelet transform (WT) of the k3-weighted Fe K edge EXAFS, Fourier transform (FT) of the Fe K edge EXAFS spectrum in R and k space and the corresponding fitting curve for SAC-FeN-WPC, Fourier transform (FT) of the Fe K edge EXAFS spectrum in R and k space and the corresponding fitting curve for iron phthalocyanine (FePc), Fourier transform (FT) of the Fe K edge EXAFS spectrum in R and k space and the corresponding fitting curve for Fe foil, Fourier transform (FT) of the Fe K edge EXAFS spectrum in R and k space and the corresponding fitting curve for Fe2O3, LSV ORR and OER curves for SAC-FeN-WPC before etching and SAC-FeN-WPC, LSV curves at different rotation rates for SAC-FeN-WPC and K-L plots at different potentials of SAC-FeN-WPC, LSV ORR curves at a rotating rate of 1600 rpm for SAC-FeN-WPC-2:1, SA-FeN-WPC-1:1, SA-FeN-WPC-1:2, SA-FeN-WPC-800, SA-FeN-WPC-900, and SA-FeN-WPC-1000, chronoamperometric curves for the OER of SAC-FeN-WPC in an O2-saturated 0.1 M KOH aqueous solution at 1600 rpm, N 1s high-resolution XPS spectra of SAC-FeN-WPC before and after an OER i–t test and the contents of different N species in SAC-FeN-WPC before and after an OER i–t test, LSV ORR curves at a rotation rate of 1600 rpm for SAC-FeN-WPC, AlCl3-N-WPC, and ZnCl2-N-WPC, LSV OER curves at a rotation rate of 1600 rpm for SA-FeN-WPC, AlCl3-N-WPC, and ZnCl2-N-WPC, open-circuit plots of SAC-FeN-WPC- and Pt/C+RuO2-based ZABs, open-circuit plots of a SAC-FeN-WPC plate, galvanostatic discharge/charge cycling curves at 10 mA cm–2, BET surface area, pore volume, and elemental contents of catalysts, room-temperature 57Fe Mössbauer parameters for SAC-57FeN-WPC, and a summary of the catalytic activities of the reported composite electrocatalysts in 0.1 M KOH (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology,energy & fuels,electrochemistry