The effect of rare-earth oxides on the energy storage performances in BaTiO₃ based ceramics

Qinghuan Huang,Feng Si,Bin Tang

DOI: https://doi.org/10.1016/j.ceramint.2022.02.299

IF: 5.532

2022-01-01

Ceramics International

Abstract:In this work, 0.7BaTiO3-0.3Sr0.2Bi0.7TiO3 (0.7BT-0.3SBT) ceramics with 0.15 mol% various rare-earth oxides doped are designed and synthesized by the conventional solid-state route. All prepared samples exhibited a single perovskite phase and dense microstructure with fine grain size (0.2-0.5 mu m) after sintering at 1180 degrees C. Especially, the Gd-doped 0.7BT-0.3SBT ceramics exhibited excellent energy storage performances; the corresponding recoverable energy density and efficiency were 3.2 J/cm3 and 91.5% under an electric field of 330 kV/cm, respectively. Meanwhile, doping with Gd caused the BT-based ceramics to possess excellent temperature (30-150 degrees C) and outstanding frequency stabilities (10-1000 Hz). Moreover, the pulsed charge-discharge experiments revealed that a high power density of 59 MW/cm3 and a fast discharge speed of 110 ns with outstanding temperature stability could be synchronously obtained in the Gd-doped composition. All these features are attractive for pulsed power applications.