Abstract:Random and block copolymers of 2-methoxyethyl vinyl ether (MOVE) and 2-ethoxyethyl vinyl ether (EOVE) were synthesized within 180 s via IBVE-HCl/SnCl 4 initiating system in the presence of THF in a microflow system. The polymers can be produced continuously and efficiently with extremely narrow molecular weight distributions ( M w / M n =1.09–1.18) even at the existence of pendant oxyethylene units. Polymerization rate can be accelerated by reducing THF to very low concentration ([THF]=50 mmol/L), reaching conversions over 60% and 70% in 60 s for EOVE and MOVE, respectively. Random copolymers poly(MOVE 100 x − r -EOVE 100(1− x ) ) ( x =0.25, 0.5, 0.75) experienced very sensitive phase separation process, of which phase separation temperature ( T ps ) can be adjusted between 20 and 70 °C by controlling monomer composition. On the other hand, thermally induced phase separation of diblock copolymers poly(MOVE 100 - b -EOVE 100 ) was not so sensitive as its random copolymer counterpart. Relatively bigger difference between phase separation temperatures of heating and cooling process (Δ T ps ) was found for diblock copolymer.

Living Copolymerization of EOVE and MOVE: Fast Flow Synthesis and Thermal Responsive Behavior