Abstract:One of the long-standing challenges in experimental physics is the observation of room-temperature superconductivity1,2. Recently, high-temperature conventional superconductivity in hydrogen-rich materials has been reported in several systems under high pressure3–5. An important discovery leading to room-temperature superconductivity is the pressure-driven disproportionation of hydrogen sulfide (H2S) to H3S, with a confirmed transition temperature of 203 kelvin at 155 gigapascals3,6. Both H2S and CH4 readily mix with hydrogen to form guest–host structures at lower pressures7, and are of comparable size at 4 gigapascals. By introducing methane at low pressures into the H2S + H2 precursor mixture for H3S, molecular exchange is allowed within a large assemblage of van der Waals solids that are hydrogen-rich with H2 inclusions; these guest–host structures become the building blocks of superconducting compounds at extreme conditions. Here we report superconductivity in a photochemically transformed carbonaceous sulfur hydride system, starting from elemental precursors, with a maximum superconducting transition temperature of 287.7 ± 1.2 kelvin (about 15 degrees Celsius) achieved at 267 ± 10 gigapascals. The superconducting state is observed over a broad pressure range in the diamond anvil cell, from 140 to 275 gigapascals, with a sharp upturn in transition temperature above 220 gigapascals. Superconductivity is established by the observation of zero resistance, a magnetic susceptibility of up to 190 gigapascals, and reduction of the transition temperature under an external magnetic field of up to 9 tesla, with an upper critical magnetic field of about 62 tesla according to the Ginzburg–Landau model at zero temperature. The light, quantum nature of hydrogen limits the structural and stoichiometric determination of the system by X-ray scattering techniques, but Raman spectroscopy is used to probe the chemical and structural transformations before metallization. The introduction of chemical tuning within our ternary system could enable the preservation of the properties of room-temperature superconductivity at lower pressures. Room-temperature superconductivity is observed in a photochemically synthesized ternary carbonaceous sulfur hydride system at 15 °C and 267 GPa.

Crystal structures and superconductivity of carbonaceous sulfur hydrides at pressures up to 300 GPa

High-temperature Superconductivity in Sulfur Hydride Evidenced by Alternating-Current Magnetic Susceptibility

Enhanced superconductivity in C-S-H compounds at high pressure

Synthesis and structure of carbon doped H3S compounds at high pressure

Superconductivity determined by the S–H framework in CH4-inserted S–H framework hydrides under high pressures

Missing theoretical evidence for conventional room temperature superconductivity in low enthalpy structures of carbonaceous sulfur hydrides

Room-temperature superconductivity in a carbonaceous sulfur hydride

A Little Bit of Carbon Can do a Lot for Superconductivity in H$_3$S

Structural evolution and molecular dissociation of H<sub>2</sub>S under high pressures

Pressure-induced hydride superconductors above 200 K

Hydrogen sulfide at high pressure: change in stoichiometry

Effect of van Hove singularities on high-Tc superconductivity in H3S

High-pressure synthesis of a ternary yttrium-sulfur hydride superconductor with a high Tc of approximately 235 K

Search for high-Tc conventional superconductivity at megabar pressures in the lithium-sulfur system

Superconductive "sodalite"-like clathrate calcium hydride at high pressures

The metallization and superconductivity of dense hydrogen sulfide

Hydrogen‐rich Superconductors at High Pressures

Phase Diagram and High-Temperature Superconductivity of Compressed Selenium Hydrides

Photochemical Synthesis of P-S-H Ternary Hydride at High Pressures

Prediction of high- T c superconductivity in H 6 S X ( X = Cl , Br ) at pressures below one megabar

High-Te Superconductivity in Squeezed Cubic CSeH6 and C2TeH8 Ternary Polyhydrides