Evaluation and Mechanisms of Internal Stress Development in High-Build Epoxy Protective Coatings During Thermal Cycling

Weiwei Li,Chunyang Wei,Jiyun Tang,Zongkui Li,Xiaowei An,Qi Li,Jingjing Wang,Liwei Liu

DOI: https://doi.org/10.1016/j.porgcoat.2022.106898

IF: 6.6

2022-01-01

Progress in Organic Coatings

Abstract:Long-term protection in highly corrosive environments has advanced to use high-solid coatings with high thickness, known as high-build coatings. However, these coatings were found to be more susceptible to cracking and delamination failures in-service with temperature variations. To understand how a high-build film is stressed at different temperatures, we developed an efficient measurement method by employing imaging scanning device and image analysis to quantitatively evaluate internal stress in two purposely formulated epoxy coatings with different elasticities through 30 thermal cycles between -25 to 50 ?. The results showed that the magnitude of internal stress was dependent on the coating elasticity, film thickness, and the difference in coefficient of linear thermal expansion (CTE) between the coating and its substrate apart from the service temperature and the thermal cycles. Moreover, thicker coating develops a significantly higher internal stress, which explains why cracking or delamination is typically associated with excessively thick coatings. The investigated mechanisms of the stress development during thermal cycling will be a useful guide to formulate mechanically durable high-build coatings.