Abstract:Among metals used for CO2 electroreduction in water, Cu appears to be unique in its ability to produce C2+ products like ethylene. Bimetallic combinations of Cu with other metals have been investigated with the goal of steering selectivity via creating a tandem pathway through the CO intermediate or by changing the surface electronic structure. Here, we demonstrate a facile cation exchange method to synthesize Ag/Cu electrocatalysts for CO2reduction using Cu sulfides as a growth template. Beginning with Cu2−xS nanosheets (C?nano-0, 100 nm lateral dimension, 10 nm thick), varying the Ag+concentration in the exchange solution produces a gradual change in crystal structure from Cu7S4 to Ag2S, as the Ag/Cu mass ratio varies from 0.1 to 10 (CA-nano-x, x indicating increasing Ag fraction). After cation exchange, the nanosheet morphology remains but with increased shape distortion as the Ag fraction is increased. Interestingly, the control (C-nano-0) and cation exchanged nanosheets have very high Faradaic efficiency for producing formate at low overpotential (−0.2 V vs. RHE). The primary effect of Ag incorporation is increased production of C2+ products at −1.0 V vs. RHE compared with C-nano-0, which primarilyproduces formate. Cation exchange can also be used to modify the surface of Cu foils. A two-step electro-oxidation/sulfurization process was used to form Cu sulfides on Cu foil(C-foil-x) to a depth of a few 10s of microns. With lower Ag+concentrations, cation exchange produces uniformly dispersed Ag; however, at higher concentrations, Agparticles nucleate on the surface. During CO2 electroreduction testing, the product distribution for Ag/Cu sulfides on Cu foil (CA-foil-x-y) changes in time with an initial increase in ethylene and methane production followed by a decrease as more H2 is produced. The catalysts undergo a morphology evolution towards a nest-like structure which could be responsible for the change in selectivity. For cation-exchanged nanosheets (CA-nano-x), pre-reduction at negative potentials increases the CO2 reduction selectivity compared to tests of as-synthesized material, although this led to the aggregation of nanosheets into filaments. Both types of bimetallic catalysts are capable of selective reduction of CO2 to multi-carbon products, although the optimal configurations appear to be metastable.

Poly(ionic Liquid)-Based Bimetallic Tandem Catalysts for Highly Efficient Carbon Dioxide Electroreduction

Highly Efficient Electrocatalytic CO2 Reduction to C2+ Products on a Poly(ionic liquid)-Based Cu-0-Cu-I Tandem Catalyst

Highly Efficient Electrocatalytic CO<sub>2</sub> Reduction to C<sub>2+</sub> Products on a Poly(ionic liquid)‐Based Cu<sup>0</sup>–Cu<sup>I</sup> Tandem Catalyst

Electroreduction of carbon dioxide to multi-electron reduction products using poly(ionic liquid)-based Cu-Pd catalyst

Stabilizing High‐Valence Copper(I) Sites with Cu–Ni Interfaces Enhances Electroreduction of CO2 to C2+ Products

Poly(Ionic Liquid) Boosts Overall Performance of Electrocatalytic Reduction of Low Concentration of Co Gas

Sn-based Redox Cycle Mediated Microenvironment Regulation of Cu Sites on Poly(ionic Liquid) Enhance Electrocatalytic CO-to-C2+conversion

Regulating Electrochemical CO2RR Selectivity at Industrial Current Densities by Structuring Copper@poly(ionic Liquid) Interface

Microenvironment Regulation for High-Performance Acidic CO2 Electroreduction on Poly(ionic Liquid)-Modified Cu Surface

Bimetallic Cu-Bi catalysts for efficient electroreduction of CO2 to formate

Efficient Electrocatalytic Reduction of CO2 to CO on Highly Dispersed Ag Nanoparticles Confined by Poly(ionic Liquid)

N-Heterocyclic Carbene Coordinated Cu Single Atoms on Poly(ionic Liquid) for Selective Electroreduction of CO 2 to CH 4 at High Current Density

Tandem Electrocatalytic CO2 Reduction with Efficient Intermediate Conversion over Pyramid-Textured Cu-Ag Catalysts

Synergistic Geometric and Electronic Effects in Bi–Cu Bimetallic Catalysts for CO 2 Electroreduction to Formate over a Wide Potential Window

A Bimetallic Ag/Ti‐Based Coordination Polymer As a Catalyst for Electrocatalytic CO2 Reduction and Selective Sulfide Oxidation

Poly(ionic Liquid)s with High Density of Nucleophile /electrophile for CO2 Fixation to Cyclic Carbonates at Mild Conditions

Copper Sulfide As the Cation Exchange Template for Synthesis of Bimetallic Catalysts for CO2 Electroreduction

Bifunctional poly(ionic liquid) catalyst with dual-active-center for CO2 conversion: Synergistic effect of triazine and imidazolium motifs

Mesoporous palladium–copper bimetallic electrodes for selective electrocatalytic reduction of aqueous CO2 to CO

Highly Selective Palladium-Copper Bimetallic Electrocatalysts for the Electrochemical Reduction of CO2 to CO