Unraveling Structure Evolution Failure Mechanism in MoS2 Anode for Improving Lithium Storage Stability

Guannan Zu,Shiyu Xu,Changhao Wang,Hongyi Li,Manchen Zhang,Xiaoxing Ke,Yuxiang Hu,Ruzhi Wang,Jinshu Wang

DOI: https://doi.org/10.1016/j.jmst.2022.04.016

2022-01-01

Abstract:2H phase molybdenum disulfide(2H-MoS2)possesses the two-dimensional layered structure and high theoretical capacity,presenting excellent lithiation-delithiation property.However,the violent capacity decay within dozens of cycles still remains a great challenge due to lacking of in-depth failure mech-anism.Herein,a novel decay-recovery-decay failure phenomenon upon long-term cycles is reported for the first time,which originates from the slow size change of Mo nanoparticles(NPs).Decay stages are triggered by many irregular-shaped Mo NPs with the increasing size up to～15 nm,leading to prominent pseudocapacitance failure and capacity loss.Subsequent recovery stages are attributed to the pulveriza-tion of coarse Mo NPs through surface sulfurization and accompanying lithiation.To overcome the insta-bility issue,proper modifiers should be introduced to restrain the spontaneous growth of Mo NPs,such as aluminum oxide(Al2O3).The strong Mo-Al2O3 bond gradually"drags"Al2O3 fragments into the active material as the cycle continuously proceeds,resulting in the efficient refinement and the reversible con-version between Mo and MoS2.Therefore,the enhanced cycling stability and the capacity retention are successfully achieved.It is expected to provide a new insight into the energy storage of transition metal chalcogenide anode materials in rechargeable batteries.