Abstract:Violet phosphorus is the most stable phosphorus allotrope with a layered structure. The corresponding violet phosphorene, a more stable two-dimensional semiconducting structure than black phosphorene, is a promising two-dimensional material for electronic and optoelectronic devices. The synthesis of violet phosphorus is the key factor to its experimental research. However, no clear evidence has been reported for the synthesis of violet phosphorus since its first proposal in 1865. The violet phosphorus was even debated to be a metastable intermediate phase. Until recently, the violet phosphorus crystals have just been successfully produced and exfoliated to give violet phosphorene. High yield synthesis of highly crystalline and pure violet phosphorus is crucial for the further exploration of violet phosphorus and phosphorene. In this work, highly crystalline and pure violet phosphorus crystals have been produced with a yield as high as 80%. The vapor transport, nucleation, crystal growth conditions, and synthesis mechanism have been studied to obtain violet phosphorus instead of black phosphorus. The mixture of transport agents and amorphous red phosphorus was heated to 600 °C to form P–Sn–I vapor and transported to the cooler zone (580 °C). The phosphorus was separated out from the P–Sn–I composites after cooling down to 530 °C to form violet phosphorus nuclei. The nucleation time and further cooling time correspond to the amount and crystallinity of violet phosphorus crystals. The precipitation has been demonstrated to be SnI2 crystals with a space group of C2/m (12) after the growth of violet phosphorus crystals. The synthesis of highly crystalline and pure violet phosphorus with high yield provides the application possibility of violet phosphorus and phosphorene in mechanic, electronic, optoelectronic, catalysts, and medical fields.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.0c02273?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.0c02273</a>.Powder XRD spectra and X-ray rocking curve of the (004) diffraction of VP crystals (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.0c02273/suppl_file/cm0c02273_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Solution Phase Synthesis of the Less-Known Form II Crystalline Red Phosphorus

Ultra-Long Crystalline Red Phosphorus Nanowires from Amorphous Red Phosphorus Thin Films.

Assessing the Structural Diversity of Form II Red Phosphorus via Stepwise Crystal Structure Search

Wet chemical synthesis of type-II red phosphorus and evaluation of its photocatalytic activity using a non-dye degradation method

Polymorphic Development Strategy for Rapid Pesticide Release: A Case Study of Spirotetramat

High Electron Mobility of Amorphous Red Phosphorus Thin Films

Red Phosphorus in Its Two-Dimensional Limit: Novel Clathrates with Varying Band Gaps and Superior Chemical Stabilities.

Controllable preparation of crystalline red phosphorus and its photocatalytic properties

Polarization conversion in bottom-up grown quasi-1D fibrous red phosphorus flakes

Crystalline red phosphorus for selective photocatalytic reduction of CO<sub>2</sub> into CO

Type-II Red Phosphorus: Wavy Packing of Twisted Pentagonal Tubes

Structure and Bonding in Amorphous Red Phosphorus

Hittorf'S Phosphorus: the Missing Link During Transformation of Red Phosphorus to Black Phosphorus

High Yield Synthesis of Violet Phosphorus Crystals

Triclinic La7Zn2P11 with P3–, P24–, and P35– units: A combined study by 31P solid-state NMR spectroscopy and single crystal X-ray diffraction

Hetero-phase dendritic elemental phosphorus for visible light photocatalytic hydrogen generation

Epitaxial Growth of Single Layer Blue Phosphorus: A New Phase of Two-Dimensional Phosphorus.

Enhanced Catalytic Activity of Crystalline Phosphorus Nanosheets Fabricated via Solvothermal Phase Transformation

Access and in situ Growth of Phosphorene-Precursor Black Phosphorus

Formation of a P 16 2- Ink from Elemental Red Phosphorus in a Thiol-Amine Mixture

Polymorph and Phase Discrimination of Lead Chromate Pigments by a Facile Room Temperature Precipitation Reaction