Promoting the activation of H 2 O via vacancy defects over metal-organic framework-derived cobalt oxide for enhanced oxygen evolution
Cheng-Zong Yuan,Hong-Rui Zhao,Si-Yu Huang,Lunliang Zhang,Jiang Li,Yao Weng,Zhong-Ti Sun,Xiaomeng Zhang,Shufeng Ye,Yunfa Chen
DOI: https://doi.org/10.1016/j.ijhydene.2023.04.279
IF: 7.2
2023-05-25
International Journal of Hydrogen Energy
Abstract:Engineering the electronic structures of transition metal oxides via vacancy defects is an efficient approach to enhance their catalytic performances, while facilely creating vacancy defects and deeply exploring the effects still remain challenging. Herein, a facile reduction method was applied to introduce oxygen vacancy defects into metal-organic frameworks (MOFs)-derived cobalt oxide (Co 3 O 4 ) polyhedron. Using zeolitic imidazolate framework-67 (ZIF-67) as Co source and self-sacrificial template, Co 3 O 4 with polyhedron morphology and porous structure was synthesized, and then oxygen vacancy defects were introduced into the as-prepared Co 3 O 4 through one-step NaBH 4 reduction treatment. Strikingly, the obtained electrocatalyst (denoted as Co 3 O 4-x ) exhibited a larger current density (112.9 mA cm −2 vs. 1.75 V), a lower overpotential (335 mV at 10 mA cm −2 ) and a smaller Tafel slope (83 mV dec −1 ) than the Co 3 O 4 , which is even superior to the state-of-the-art IrO 2 catalyst. Moreover, experiment results combined with density-functional theory (DFT) calculations revealed that the existence of oxygen vacancies could improve the conductivity, promote the activation of H 2 O and reduce the potential of potential-limited step (PLS), thus greatly boosting electrocatalytic oxygen evolution reaction (OER) performances. This work reported a strategy for preparing defect-rich OER electrocatalysts, and also provided a deep understanding of the defect effects on catalytic performances.
energy & fuels,electrochemistry,chemistry, physical