Flame Retardancy and Chemical Degradation of Epoxy Containing Phenylphosphonate Group under Mild Conditions

Chao Ma,Zhenghong Guo,Zhengping Fang,Juan Li
DOI: https://doi.org/10.1016/j.compositesb.2022.109967
IF: 11.322
2022-01-01
Composites Part B Engineering
Abstract:The development of methods for recycling of thermosetting resin is difficult due to their structure. To regulate the flame retardancy and chemical degradation behavior of epoxy (EP), a phenylphosphonate based EP monomer (DGEP) was prepared and cured using 4,4-diamino diphenylmethane (DDM). For comparison, bisphenol A EP (DGEBA/DDM) was also prepared. The modes of flame retardancy and chemical degradation have been investigated. The DGEP/DDM displays a UL-94 V0 rating while the DGEBA/DDM may not be classified in the UL-94 test. Moreover, DGEP/DDM is stable in most solvents and is degraded after 40 min in a solution of methanol/sodium hydroxide (NaOH)/water (H2O) at 50 degrees C, while DGEBA/DDM is stable under the same conditions. Degradation occurs by hydrolysis and alcoholics of phenylphosphonate in the main chain of EP under alkaline conditions. In addition, DGEP/DDM has a similar glass transition temperature and tensile properties as those for DGEBA/DDM. The introduction of phenylphosphonate into EP may represent a useful method for the preparation of flame retardant and recyclable EP. C
What problem does this paper attempt to address?