06/00140 Preparation and characterization of PtSn/C anodeelectrocatalysts for direct ethanol fuel cell

姜鲁华,周振华,周卫江,李文震,宋树芹,李焕巧,孙公权,辛勤

DOI: https://doi.org/10.1016/s0140-6701(06)80140-2

2006-01-01

Fuel and Energy Abstracts

Abstract:Highly active PtSn/C catalyst was prepared by a polyol method. The catalyst was reduced in H2/Ar atmosphere at 600 oC for 2 hours in order to obtain different metallic phase. TEM images show uniform dispersion of spherical metal nanoparticles with average diameters of 1.8 nm and 3.9 nm for the as-prepared and treated catalysts, respectively. UV/VIS spectrophotometer is employed to monitor the preparation process and the results show that Pt-Sn complex formed once the precursors of Pt and Sn were mixed. The structure properties of the samples were characterized using X-ray diffraction. The results show that after reduction, the catalyst tends to form PtSn alloy. TPR experiment results show that Sn exists in multivalent state in the as-prepared sample while only zero-valence Sn was detected in the treated sample. Cyclic voltammety (CV) technique and single direct ethanol fuel cell (DEFC) tests indicate that the as-prepared catalyst possesses superior catalytic activity for ethanol oxidation to the treated sample. The results suggest that Pt and multivalence Sn are the active species for ethanol oxidation.