In Situ Investigations of Li‐MoS2 with Planar Batteries
Jiayu Wan,Wenzhong Bao,Yang Liu,Jiaqi Dai,Fei Shen,Lihui Zhou,Xinghan Cai,Daniel Urban,Yuanyuan Li,Katherine Jungjohann,Michael S. Fuhrer,Liangbing Hu
DOI: https://doi.org/10.1002/aenm.201401742
IF: 27.8
2014-01-01
Advanced Energy Materials
Abstract:J. Wan, Dr. W. Bao, J. Dai, F. Shen, Dr. L. Zhou, D. Urban, Y. Li, Dr. K. Jungjohann, Prof. L. Hu Department of Materials Science and Engineering University of Maryland College Park , MD 20742-4111 , USA E-mail: binghu@umd.edu Dr. W. Bao, X. Cai, Prof. M. S. Fuhrer Department of Physics University of Maryland College Park , MD 20742-4111 , USA Dr. Y. Liu, Dr. K. Jungjohann Center for Integrated Nanotechnologies (CINT) Sandia National Laboratories Albuquerque , NM 87185 , USA Prof. M. S. Fuhrer School of Physics Monash University Victoria 3800 , Australia E-mail: michael.fuhrer@monash.edu DOI: 10.1002/aenm.201401742 We have designed a planar microbattery that allows in situ electrical transport measurement during electrochemical charge and discharge in micron-sized individual crystallites of 2D-layered nanosheets, as well as optical studies (transmittance, Raman spectroscopy), which can give information about the electronic structure of the active material. To demonstrate the utility of our microbattery platform, we study the lithiation of MoS 2 crystallites. We observe that the electrical conductivity of the 2D MoS 2 crystallites is highly dependent on thickness and the rate of lithiation in the fi rst cycle. We use in situ TEM to confi rm that upon rapid fi rst-cycle lithiation the formation of a Mo conductive network imbedded in the Li 2 S matrix leads to an enhanced electrical conductivity compared to the pristine MoS 2 . We applied the results in Li-MoS 2 coin cells with composite electrodes, demonstrating that batteries with fast lithiation on the fi rst cycle showed signifi cantly higher specifi c capacity than batteries lithiated slowly. The microbattery platform can be generally applied to other energy storage materials and a wide range of characterization techniques, and is thus a powerful tool to uncover the properties of nanoscale materials undergoing electrochemical modifi cation. As in the example demonstrated here, we expect this platform will lead to new insights into the operation of battery materials at the nanoscale, leading to new strategies in improving the cell performance. A schematic crystal structure of 2H-MoS 2 is illustrated in Figure 1 a, with the lattice parameters a = 3.16 Å and c = 12.29 Å. Our microbattery platform developed for the in situ measurement of the optical transmittance and electrical transport of 2D nanomaterials is illustrated in Figure 1 b. A MoS 2 crystal and lithium metal are deposited on top of the Cu transport electrodes and current collector, respectively. The MoS 2 fl ake can be charged/discharged by connecting transport electrodes and current collector to an electrochemical workstation. Coupling the microbattery with a transmission optical microscope/probe station, we can then carry out in situ optical transmittance and electrical transport measurements on the same MoS 2 crystal. Optical images of uniform-thickness mechanically exfoliated MoS 2 crystals are shown in Figure 1 c,d, with dimensions as large as 100 μm × 100 μm. We used atomic force microscopy (AFM) to determine the morphology and thickness of exfoliated MoS 2 , in Figure 1 e,f. A photograph of the complete microbattery device is shown in Figure 1 g. The region of the transport electrodes is expanded in Figure 1 h, showing a large uniform area of MoS 2 crystal spanning the electrodes. To understand the intrinsic resistance change during lithiation, an in situ electrical transport measurement was carried out using our microbattery setup. Figure 2 a shows the simultaneously measured resistance and electrochemical potential at a small constant lithiation current at 0.5 μA for a single MoS 2 crystal of thickness 35 nm. Figure 2 a (inset) illustrates the MoS 2 is an earth-abundant mineral material that has been widely studied for its many applications such as lubrication, hydrodesulfurization catalysis, and as an electrical energy storage electrode. [ 1–3 ] Recently, 2D MoS 2 crystals have attracted tremendous research interest for their unique properties in photonics, optoelectronics, electronics, and energy applications. [ 4–12 ] Liquidphase exfoliation of layered materials can provide an excellent approach for mass production of 2D materials, [ 13–15 ] enabling applications that require a large quantity of materials, particularly electrical energy storage. Indeed, the large van der Waals gap of MoS 2 enables excellent electrochemical performance, and MoS 2 -based Li-ion, Na-ion, and Mg-ion batteries are being explored for electric vehicles and grid-scale storage. [ 16–25 ]