Promotion of Cartilage Extracellular Matrix by Anti-Inflammatory Peptides-Loaded Zirconium Metal-Organic Frameworks Encapsulated in Hydrogels

QIN Xiaoping,LI Tao,CHEN Cheng,YANG Liu

DOI: https://doi.org/10.16016/j.2097-0927.202111169

2022-01-01

Abstract:Objective To prepare a hydrogel scaffold with cartilage regeneration and inflammatory microenvironment control capacity for chondrodefects treatment in osteoarthritis. Methods The zirconium metal-organic framework (Zr MOF) was prepared by solvothermal synthesis and then loaded with anti-inflammatory peptide KAFAK. The pullulan/polyethylene glycol composite hydrogel was prepared by UV crosslinking. Then the obtained Zr MOF was encapsulated in the hydrogel. Then the physicochemical properties of the hydrogel were characterized by scanning electron microscopy (SEM), swelling equilibrium, degradation experiments and rheological and mechanical studies. Rabbit bone mesenchymal stem cells (BMSCs) were used as seed cells. The bioactivity of the hydrogel and the content of glycosaminoglycans in the extracellular matrix were tested by live/dead staining. The expression of chondrogenic genes COL2A1 and ACAN, and hypertrophic gene COL10A1 was measured with RT-PCR. Results After being loaded with anti-inflammatory peptide KAFAK to Zr MOF, the hydrated particle exhibits a size of 352.5 nm, a particle size distribution (PDI) of 0.29, and a zeta potential of 18.27±0.55 mV. After the encapsulation of Zr MOF, when the content of Zr MOF was increased, there were more small holes in the scaffold observed by SEM, the swelling time was shortened, the degradation rate was increased and the rheological property was improved. In 21 d after KAFAK was loaded onto the Zr MOF and then encapsulated with hydrogel, the release of the peptide was (84.1±5.0)%, indicating a good sustained release. In Gel, Gel-100 Zr MOF, and Gel-100 Zr MOF@KAFAK groups, the cell survival rates was (90.7±5.4)%, (93.5±4.3)% and (91.9±3.1)%, respectively. With rabbit BMSCs as seed cells, after 7 and 14 d of chondrogenic induction, the glycosaminoglycan in Gel-100 Zr MOF @KAFAK group was significantly higher than that in Gel and Gel-100 Zr MOF group (P < 0.05). The results of RT-PCR indicated that the expression levels of COL2A1 and ACAN were increased, whereas that of COL10A1 was decreased (P < 0.05). Conclusion KAFAK-loaded Zr MOF is successfully encapsulated in hydrogels. The hydrogels control the inflammatory microenvironment through the sustained release of KAFAK, and result in more cartilage extracellular matrix and better maintenance of chondrogenic phenotype.