Microstructure and mechanical properties of CoCrFeNiW high entropy alloys reinforced by μ phase particles
Lei Wang,Liang Wang,YingChun Tang,Lei Luo,LiangShun Luo,YanQing Su,JingJie Guo,HengZhi Fu
DOI: https://doi.org/10.1016/j.jallcom.2020.155997
IF: 6.2
2020-11-01
Journal of Alloys and Compounds
Abstract:<p>In this study, the microstructure and mechanical properties of the as-cast and as-annealed CoCrFeNiW<sub><em>x</em></sub> (<em>x</em> = 0, 0.2, 0.4 and 0.6, <em>x</em> value in molar ratio) high-entropy alloys were investigated. Both W-addition and annealing treatment were conducive to the formation of the μ phase in CoCrFeNiW<sub><em>x</em></sub> alloys. With the increase of <em>x</em> value, the microstructures of the as-cast HEAs evolved from single-phase solid solution (<em>x</em> = 0, 0.2) to hypoeutectic structure (<em>x</em> = 0.4), then to hypereutectic structure (<em>x</em> = 0.6). The as-cast CoCrFeNiW<sub>0.4</sub> alloy exhibited a tensile strength of 690.7 MPa with a considerable elongation of 33.1%, which resulted from solid solution strengthening and second phase strengthening. After annealing, the as-annealed CoCrFeNiW<sub>0.4</sub> alloy showed an increased tensile strength of 970.9 MPa, owing to the precipitation of μ-phase particles. Deformed microstructures indicated that cracks generated from μ-phase precipitates of different sizes, and suppressed by the ductile FCC solid solution. Moreover, the high-density dislocation tangles around the μ-phase precipitates lead to a high strain hardening rate, which improved the strength significantly.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering