Construction of hierarchical proton sieving-conductive channels in sulfated UIO-66 grafted polybenzimidazole ion conductive membrane for vanadium redox flow battery

Bo Pang,Fujun Cui,Wanting Chen,Xiaozhou Wang,Ruohan Du,Xuemei Wu,Xiaoming Yan,Yan Dai,Gaohong He

DOI: https://doi.org/10.1016/j.jpowsour.2022.231132

IF: 9.2

2022-01-01

Journal of Power Sources

Abstract:Sieving of H+/VII + ions is essential to vanadium redox flow battery (VRFB). Herein, the interconnected hierarchical proton sieving-conductive channels are constructed through the graft of sulfated UIO-66 (UIO-66OSO3) along the polybenimidazole (PBI) backbone with the highly reactive and acidic sulfate ester functional group. Highly porous UIO-660SO3 provides numerous angstrom scale sieving channels (about 5 angstrom) to transport proton and repel vanadium ion, and the sulfated groups ended flexible side chains are densely bonded to UIO-66 and aggregate into broad nanoscale ionic clusters (similar to 8 nm) for fast proton conduction between UIO-660SO3 nanoparticles. The as-prepared membrane exhibits low vanadium permeability (7.88 x 10(-9) cm(2)s(-1)) and area resistance (0.23 Omega cm(-2), lower than that of Nafion 212). High energy efficiency (86.1%) and low discharge capacity decay (0.15% per cycle) are achieved even after 100 charge-discharge cycles at 100 mA cm(-2), and the battery keeps running for 2000 cycles without morphological and chemical changes. The VRFB proprieties are far superior to Nafion 212 membrane VRFB proprieties (energy efficiency 74.9%, decay rate 0.71% per cycle), and also surpasses most recently reported porous, dense and hybrid ion conductive membranes.