Abstract:The complicated toughening mechanism of Mode II cracking in end notch flexure (ENF) test for fibrous composites prevents the existence of clear crack-tip. Hence the concept of equivalent linear crack length was proposed to avoid detecting the crack-tip in ENF test, which assumes that the increase of compliance due to the development of fracture process zone (FPZ) or crack propagation is attributed to the equivalent elastic crack length giving the same compliance as the one of the actual crack with its FPZ; thus the equivalent crack length can be estimated according to the associated compliance obtained from experiment. The objective of the presented work was to develop an analytical model for the analysis of ENF test specimen without need for crack-tip identification and complicated data reduction. Bilinear cohesive law was employed to model the cohesive force across the potential crack interfaces. Analytical solutions for the governing equation were derived. Furthermore, methods to determine the cohesive parameters, the length of fracture process zone (FPZ), and the energy release rate were developed. The critical loads corresponding to the damage and crack onset can also be estimated by the model. Experimental validation was implemented and a good agreement was achieved between the test results and model predictions. It can be concluded that bilinear cohesive law may achieve a good approximation for the tangential traction-separation constitutive relationship in Mode II fracture; the shear strength of the material can be taken as the critical stress of cracking onset; the energy release rate depends on the initial crack length to some extent, and this effect could be reduced as the length of initial crack increases.

Experimental and Numerical Analysis on Mode II Fracture Toughness of CFRP Adhesive Joints Using a Nonlinear Cohesive/friction Coupled Model

Estimation of fracture behavior of CFRP/CFRP adhesively bonded joints under mixed-mode conditions using a cohesive zone model

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

A Nonlinear Friction-Cohesive Model for Characterizing Mode II Fracture of Laminated Composites

A semi-analytical model for the mode II fracture toughness of multidirectional composite laminates

A Bi-Linear Cohesive Law-Based Model for Mode II Fracture Analysis: Application to ENF Test for Unidirectional Fibrous Composites

Determination of fracture toughness of an adhesive in civil engineering and interfacial damage analysis of carbon fiber reinforced polymer–steel structure bonded joints

A semi-analytical method for determining mode-II fracture toughness and bridging law of composite laminates

A Nonlinear Cohesive/friction Coupled Model for Shear Induced Delamination of Adhesive Composite Joint

Experimental and numerical investigation on test methods for mode II fracture of composite‐titanium adhesively bonded structures

Experimental estimation and numerical validation of cohesive zone parameters in hydroxyl functionalized MWCNTs‐reinforced CFRP under pure mode II loading

An Interface-Dependent Model of Plateau Fracture Toughness in Multidirectional CFRP Laminates under Mode I Loading

Determination of Mixed-Mode I/II Fracture Toughness and Bridging Law of Composite Laminates

Modeling Brittle Fractures in Epoxy Nanocomposites Using Extended Finite Element and Cohesive Zone Surface Methods

Enhancing Mode I Fracture Toughness Of Adhesively Bonded Unidirectional Composite Joints Using Surfactant-Stabilized Multi-Walled Carbon Nanotube And Graphene Nanoplate

Numerical modelling of the mode I fracture behavior in composite laminates with significant R-curve effect

On the Effect of Adhesive Thickness on Mode I Fracture Energy - an Experimental and Modelling Study Using a Trapezoidal Cohesive Zone Model

Mixed-mode I/II Fracture Behavior for Adhesively-Bonded Pultruded GFRP Joint under Four-Point Bending

Rate-Dependent Cohesive Models for Dynamic Mode I Interfacial Propagation and Failure of Unidirectional Composite Laminates

Evaluation of Mode II Fracture Toughness under High Loading Rate Conditions for Composite Bonded Joints

Numerical approach to fracture behavior of CFRP/concrete bonded interfaces