Abstract:A novel micro/nanoscale rough structured superhydrophilic hybrid-coated mesh that shows underwater superoleophobic behavior is fabricated by spray casting or dipping nanoparticle–polymer suspensions on stainless steel mesh substrates. Water droplets can spread over the mesh completely; meanwhile, oil droplets can roll off the mesh at low tilt angles without any penetration. Besides overcoming the oil-fouling problem of many superhydrophilic coatings, this superhydrophilic and underwater superoleophobic mesh can be used to separate oil and water. The simple method used here to prepare the organic–inorganic hybrid coatings successfully produced controllable micro-nano binary roughness and also achieved a rough topography of micro-nano binary structure by controlling the content of inorganic particles. The mechanism of oil–water separation by the superhydrophilic and superoleophobic membrane is rationalized by considering capillary mechanics. Tetraethyl orathosilicate (TEOS) as a base was used to prepare the nano-SiO2 solution as a nano-dopant through a sol-gel process, while polyvinyl alcohol (PVA) was used as the film binder and glutaraldehyde as the cross-linking agent; the mixture was dip-coated on the surface of 300-mesh stainless steel mesh to form superhydrophilic and underwater superoleophobic film. Properties of nano-SiO2 represented by infrared spectroscopy and surface topography of the film observed under scanning electron microscope (SEM) indicated that the film surface had a coarse micro–nano binary structure; the effect of nano-SiO2 doping amount on the film’s surface topography and the effect of such surface topography on hydrophilicity of the film were studied; contact angle of water on such surface was tested as 0° by the surface contact angle tester and spread quickly; the underwater contact angle to oil was 158°, showing superhydrophilic and underwater superoleophobic properties. The effect of the dosing amount of cross-linking agent to the waterproof swelling property and the permeate flux of the film were studied; the oil–water separation effect of the film to oil–water suspension and oil–water emulsion was studied too, and in both cases the separation efficiency reached 99%, which finally reduced the oil content to be lower than 50 mg/L. The effect of filtration times to permeate flux was studied, and it was found that the more hydrophilic the film was, the stronger the stain resistance would be, and the permeate flux would gradually decrease along with the increase of filtration times.

Facile strategy for the construction of a robust underbrine superoleophobic membrane for highly efficient oil-brine separation

Fabrication of a Novel Superhydrophobic and Superoleophilic Surface by One-Step Electrodeposition Method for Continuous Oil/water Separation

Superhydrophilic/underwater Superoleophobic Oil-in-water Emulsion Separation Membrane Modified by the Co-Deposition of Polydopamine and Chitosan-Tripolyphosphate Nanoparticles

Ni-Al Layered Double Hydroxides (ldhs) Coated Superhydrophobic Mesh with Flower-Like Hierarchical Structure for Oil/water Separation

Fabrication of Ph-Sensitive Superhydrophilic/Underwater Superoleophobic Poly(vinylidene Fluoride)-Graft-(sio2 Nanoparticles and PAMAM Dendrimers) Membranes for Oil-Water Separation.

High-flux Underwater Superoleophobic Hybrid Membranes for Effective Oil–water Separation from Oil-Contaminated Water

A Facile Solvent-Manipulated Mesh for Reversible Oil/Water Separation

Robust superhydrophilic and underwater superoleophobic membrane optimized by Cu doping modified metal-organic frameworks for oil-water separation and water purification

A durable Ni3S2 coated mesh with reversible transition between superhydrophobicity and underwater superoleophobicity for efficient oil-water separation

Engineering a superwettable polyolefin membrane for highly efficient oil/water separation with excellent self-cleaning and photo-catalysis degradation property

One-step fabrication of coating-free mesh with underwater superoleophobicity for highly efficient oil/water separation

Fabrication of superhydrophilic and underwater superoleophobic membranes for fast and effective oil/water separation with excellent durability

Robust bio-inspired superhydrophilic and underwater superoleophobic membranes for simultaneously fast water and oil recovery

Straightforward Oxidation of a Copper Substrate Produces an Underwater Superoleophobic Mesh for Oil/water Separation.

Fabrication of a superhydrophilic/underwater superoleophobic stainless steel mesh for oil/water separation with ultrahigh flux

A Pair of MnO2 Nanocrystal Coatings with Inverse Wettability on Metal Meshes for Efficient Oil/water Separation

A self-cleaning underwater superoleophobic mesh for oil-water separation

Controllable process to construct robust superhydrophobic membrane with tunable pore size for efficient separation of oil-water mixtures and emulsions

Micro/Nanoscale Structured Superhydrophilic and Underwater Superoleophobic Hybrid-Coated Mesh for High-Efficiency Oil/Water Separation

Robust and non-fluorinated superhydrophobic meshes with controllable pore size for high-efficiency water-in-oil emulsion separation

A rapid two-step process to prepare a high-throughput, efficient, reusable superhydrophobic–superoleophilic stainless steel mesh for oil/water separation