Enhancement of Low-temperature Brittleness of Isotactic Polypropylene Filled with Thermoplastic Elastomer for HVDC Cables

Ling Zhang,Wangsong Wu,Yuxuan Xu,Yuanxiang Zhou

DOI: https://doi.org/10.1109/EIC49891.2021.9612378

2021-01-01

Abstract:Because of its excellent heat resistance and insulation property, thermoplastic iPP is expected to replace XLPE material as the next generation of high-performance insulating materials for HVDC cables. However, iPP has the disadvantages of insufficient flexibility at room temperature and poor toughness at low temperature. Herein, 25 wt. % EPDM, POE, and SEBS elastomer were added into iPP matrices to improve its mechanical toughness, respectively. Low-temperature brittleness testing system and pulsed electroacoustic measurement system were used to analyze the mechanical properties and space charge characteristics of iPP composites. The results show that the low-temperature brittleness property of iPP/elastomer composites has been significantly improved, and the brittle fracture temperature has dropped from -8 degrees C of pure iPP to -66 degrees C, -32 degrees C, and-22 degrees C respectively. Space charge accumulation of iPP/elastomer composites are higher than those of pure iPP under -30 kV/mm. The improvement of tensile property and low-temperature brittleness of iPP/EPDM are the highest, and iPP/POE composites have the best room temperature flexibility and the least space charge accumulation. On the whole, iPP/POE composites achieves a good balance in mechanical and space charge properties.