Influence of the key factors on the performance of steel slag-desulphurisation gypsum-based hydration-carbonation materials

Xinlei Wei,Wen Ni,Siqi Zhang,Xue Wang,Jiajie Li,Huihui Du

DOI: https://doi.org/10.1016/j.jobe.2021.103591

IF: 7.144

2022-01-01

Journal of Building Engineering

Abstract:This study focuses on the influence of liquid-solid ratio, carbonation time and curing method on the carbonation reaction, and then mainly discusses the carbonation effects of four curing methods and reaction mechanisms to improve the carbonation efficiency of steel slag (SS)-desulphurisation gypsum (DG) and the strength of carbonated products. The results showed that the compressive strength of the SS-DG samples could be increased to 57.56 MPa by optimising the liquid-solid ratio to 1:5, carbonation time to 12 h, and curing method to 1dW (hydration for 1 d) + 2 dC (carbonation for 2 d). Furthermore, the compressive strength of samples cured for 1dW+2dC could increase by 33.40% compared to that cured for 2dC. The predominant mineral phases that react with CO2 in steel slag were dicalcium and tricalcium silicates, according to microanalysis (including XRD, TG-DTA, SEM-EDS and FTIR). Approximately 8% ettringite and 5% Ca(OH)(2) could be generated during the hydration process and they would be then further carbonated to afford CaCO3. In the curing process, the method of hydration followed by carbonation considerably promoted the carbonation efficiency and formation of CaCO3 by approximately 5% compared with the method of direct carbonation. The overall time of hydration and carbonation was the same while the sequencing was different; the reactants CaCO3 obtained from the curing method of 1 dW + 2 dC was increased by 2% compared with the curing method of 1dC + 1dW + 1dC, which further indicated that the curing method of hydration and then carbonation could better improve the carbonation reaction efficiency.