The Tensile Creep Behavior of a B4C-bearing High Nb Containing TiAl Alloy

Shulong Xiao,Zhenquan Liang,Yunfei Zheng,Hao Zhao,Yingfei Guo,Lijuan Xu,Xiang Xue,Jing Tian,Yuyong Chen

DOI: https://doi.org/10.1016/j.intermet.2021.107410

IF: 4.075

2022-01-01

Intermetallics

Abstract:In the present paper, the effect of B4C addition on elevated temperature tensile properties and creep resistance of as-cast Ti-43Al-6Nb-1Mo-1Cr alloy has been characterized. Experimental results reveal that 0.2 at. % B4C can improve the ultimate tensile strength and elongation of alloy at 800 degrees C. The steady-state creep rate of alloy with the addition of B4C decreases from 2.3 x 10(-6) s(-1) to 5.2 x 10(-7) s(-1) at 800 degrees C under 300 MPa. The stress exponent (n) and the apparent activation energy (Q(C)) of alloy with the addition of B4C are measured to be 3.18 at 800.C and 416.410 kJ/mol under 300 MPa, respectively. Combining microstructure observation, the dominant creep deformation mechanisms of Ti-43Al-6Nb-1Mo-1Cr-0.2B4C alloy at 800 degrees C under 300 MPa are mechanical twinning and dislocation slipping pinned by solute carbon atoms. During creep, the alpha(2) lamellar dissolution and alpha(2)/gamma interface migration occur simultaneously, and the dynamic recrystallization at colony boundary effectively alleviates the stress concentration resulting from dislocation pile-ups. In addition, the initiation of cavities as well as the propagation and coalescence of cracks are the main creep fracture features. Particularly, TiB can prevent dislocation motion and prolong the crack propagation path to increase creep resistance.