Combined Effect of Β-Nucleating Agent and Multi-Walled Carbon Nanotubes on Polymorphic Composition and Morphology of Isotactic Polypropylene
Nan Zhang,Qin Zhang,Ke Wang,Hua Deng,Qiang Fu
DOI: https://doi.org/10.1007/s10973-011-1637-z
IF: 4.755
2012-01-01
Journal of Thermal Analysis and Calorimetry
Abstract:The effects of nucleating duality, imposed by a mixed nucleating agent (NA) system containing multi-walled carbon nanotubes (MWCNTs) and a rare earth (WBG), on the crystallization behaviors of isotactic polypropylene (iPP) including the peak temperature of crystallization (T cp), polymorphic composition, and crystalline morphology, were probed in detail by calorimetry, X-ray diffraction, and polarized light microscopy. In such mixed nucleating agent system, MWCNTs is active filler to induce α-nucleation for iPP, while WBG serves as β-nucleating agent. When the WBG content was low (0.05%), the crystals of WBG were as a form of individual isotropic dendrite, and the enhancement of T cp was achieved by the incorporation of MWCNTs. As the WBG content was high as 0.1%, a percolated NA network consisted of needlelike crystals of WBG yielded before nucleating the prevalent crystallization of iPP. In this case, the addition of MWCNTs has no obvious effect on T cp. However, by varying the mass proportion of MWCNTs/WBG, the polymorphic composition was adjusted significantly, indicating a nucleation competition between MWCNTs and WBG. Although the competitive growth existed between α-crystals nucleated by MWCNTs and β-crystals nucleated by WBG, the formation of primary β-crystallite was always prior to the α-nucleated crystallization, as confirmed by crystalline morphology. These findings are useful for developing a new pathway to prepare iPP-based composite with good mechanical property via the addition of mixed nucleating system containing active inorganic filler and β-nucleating agent.