Hot Tearing Susceptibility and Solidification Behavior of Mg-xGd-(4-x)Y-2Ni-0.5Zr Alloys
Xiunan Yin,Chunxia Wang,Zheng Liu,Yunfei Lao,Zhenglong Liu,Yinghao Li
DOI: https://doi.org/10.1080/10584587.2024.2322354
2024-10-17
Integrated Ferroelectrics
Abstract:The hot tearing susceptibility (HTS) of Mg-xGd-(4-x)Y-2Ni-0.5Zr ( x = 0, 1, 2, 3, 4, wt%) alloys was evaluated using a T-shape mold method. When the Gd element increased and the Y element decreased, the HTS of the alloys decreases gradually. The Mg-4Y-2Ni-0.5Zr has the highest while Mg-4Gd-2Ni-0.5Zr has the lowest HTS value. Microstructure observation reveals that the grains of the magnesium alloy were refined to a certain extent when the Gd element increased and the Y element decreased. The 'pinning' effect of the LPSO phase precipitated along the grain boundary effectively increases the solid skeleton strength of the alloy and reduces the HTS of the magnesium alloy to a certain extent. The thin and uniform liquid film at the fracture can disperse the solidification shrinkage stress. In addition, the binary phase precipitated in the alloy forms a fast channel of residual liquid phase feeding on the liquid film, which is beneficial to feeding hot cracks. Solidification behavior of the alloys by thermal analysis showed that with the increase of the Gd element and the decrease of the Y element, the dendrite coherency temperature of the dendrites of the alloy decreases, and the residual liquid phase feeding is easier. The solid fraction of dendrite coherency increases, the skeleton strength of the alloy increases, and the HTS of the alloy decrease. In Mg-xGd-(4-x)Y-2Ni-0.5Zr ( x = 0, 1, 2, 3, 4, wt%) alloys, when x is 1, 2, 3, 4, the HTS of the alloy is reduced by 25%, 49%, 63%, 81%, respectively compared with that when x is 0.
engineering, electrical & electronic,physics, condensed matter, applied